MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究
|
左勇 1,2,3( ), 曹明鹏 1,3, 申淼 1,2, 杨新梅 1,2,3
|
Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl2-NaCl-KCl
|
ZUO Yong 1,2,3( ), CAO Mingpeng 1,3, SHEN Miao 1,2, YANG Xinmei 1,2,3
|
|
图8. 600 ℃下MNKC体系浸泡100 h后316H不锈钢截面SEM像
|
Fig.8. Cross-sectional SEM image of the 316H stainless steel exposed in molten MNKC without Mg under Ar atmosphere at 600 °C for 100 h
|
|
|
|
|