MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究
左勇1,2,3(
), 曹明鹏1,3, 申淼1,2, 杨新梅1,2,3
), 曹明鹏1,3, 申淼1,2, 杨新梅1,2,3
Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl2-NaCl-KCl
ZUO Yong1,2,3(), CAO Mingpeng1,3, SHEN Miao1,2, YANG Xinmei1,2,3
), CAO Mingpeng1,3, SHEN Miao1,2, YANG Xinmei1,2,3
图7. 600 ℃下MNKC-500 μg·g-1 Mg体系浸泡100 h后316H不锈钢截面SEM像
Fig.7. Cross-sectional SEM image of the 316H stainless steel exposed in molten MNKC-500 μg·g-1 Mg under Ar atmosphere at 600 °C for 100 h