MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究
左勇1,2,3(
), 曹明鹏1,3, 申淼1,2, 杨新梅1,2,3
), 曹明鹏1,3, 申淼1,2, 杨新梅1,2,3
Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl2-NaCl-KCl
ZUO Yong1,2,3(), CAO Mingpeng1,3, SHEN Miao1,2, YANG Xinmei1,2,3
), CAO Mingpeng1,3, SHEN Miao1,2, YANG Xinmei1,2,3
图4. 600 ℃下316H不锈钢在MNKC熔盐体系中的腐蚀电流密度随Mg添加量的变化曲线
Fig.4. Dependence of the corrosion current density of the 316H stainless steel on the amount of magnesium added into the MNKC molten salt at 600 ℃