MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究
左勇1,2,3(
), 曹明鹏1,3, 申淼1,2, 杨新梅1,2,3
), 曹明鹏1,3, 申淼1,2, 杨新梅1,2,3
Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl2-NaCl-KCl
ZUO Yong1,2,3(), CAO Mingpeng1,3, SHEN Miao1,2, YANG Xinmei1,2,3
), CAO Mingpeng1,3, SHEN Miao1,2, YANG Xinmei1,2,3
图1. 钨电极在600 ℃ MNKC熔盐体系中的循环伏安曲线
Fig.1. Cyclic voltammetric curves of MNKC molten salt on a tungsten electrode at 600 ℃ with a scan rate of 0.1 V/s