pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响
冉斗1,2, 孟惠民1, 刘星1,2, 李全德1,2,3(
), 巩秀芳2,3, 倪荣2,3, 姜英2,3, 龚显龙2,3, 戴君2,3, 隆彬2,3()
), 巩秀芳2,3, 倪荣2,3, 姜英2,3, 龚显龙2,3, 戴君2,3, 隆彬2,3()
Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions
RAN Dou1,2, MENG Huimin1, LIU Xing1,2, LI Quande1,2,3(), GONG Xiufang2,3, NI Rong2,3, JIANG Ying2,3, GONG Xianlong2,3, DAI Jun2,3, LONG Bin2,3()
), GONG Xiufang2,3, NI Rong2,3, JIANG Ying2,3, GONG Xianlong2,3, DAI Jun2,3, LONG Bin2,3()
图9. 14Cr12Ni3WMoV不锈钢在pH2和pH5的0.1 mol/L NaCl溶液中浸泡72 h后形成钝化膜的元素含量
Fig.9. Elemental percent of passive film formed on 14Cr12Ni3WMoV stainless steel after immersion in 0.1 mol/L NaCl solution with pH2 and pH5 for 72 h