冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究
张欣1,2(
), 杨光恒1, 王泽华1, 曹静1, 邵佳1, 周泽华1
), 杨光恒1, 王泽华1, 曹静1, 邵佳1, 周泽华1
Corrosion Behavior of Al-Mg-RE Alloy Wires Subjected to Different Cold Drawing Deformation
ZHANG Xin1,2(), YANG Guangheng1, WANG Zehua1, CAO Jing1, SHAO Jia1, ZHOU Zehua1
), YANG Guangheng1, WANG Zehua1, CAO Jing1, SHAO Jia1, ZHOU Zehua1
图8. 不同变形量Al-3.0%Mg-0.12%RE合金在浸泡21 d后表面形貌
Fig.8. Surface morphologies of Al-3.0%Mg-0.12%RE alloys with different strains after 21 d immersion test: (a) 51%, (b) 64%, (c) 75%, (d) 84%, (e) 91%, (f) 96%