基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为
戴明杰1,2, 刘静1,2(
), 黄峰1,2, 胡骞1,2, 李爽1
), 黄峰1,2, 胡骞1,2, 李爽1
Pitting Corrosion Behavior of X100 Pipeline Steel in a Simulated Acidic Soil Solution under Fluctuated Cathodic Protection Potentials Based on Orthogonal Method
DAI Mingjie1,2, LIU Jing1,2(), HUANG Feng1,2, HU Qian1,2, LI Shuang1
), HUANG Feng1,2, HU Qian1,2, LI Shuang1
图2. 试验后界面宏观点蚀形貌图
Fig.2. Topography views of pitting after testing: (a) A1B1C1D1, (b) A1B2C2D2, (c) A1B3C3D3, (d) A2B1C2D3, (e)A2B2C3D1, (f) A2B3C1D2, (g) A3B1C3D2, (h) A3B2C1D3, (i) A3B3C2D1