超超临界电站国产奥氏体钢C-HRA-5在超临界水中的氧化特性
方旭东1, 刘晓2, 徐芳泓1,3, 李瑞涛2, 朱忠亮2, 张乃强2(
)
)
Oxidation Behavior in Supercritical Water of Domestic Austenitic Steel C-HRA-5 for Uultra-supercritical Power Stations
FANG Xudong1, LIU Xiao2, XU Fanghong1,3, LI Ruitao2, ZHU Zhongliang2, ZHANG Naiqiang2()
)
图2. C-HRA-5钢在超临界水中氧化不同时间后氧化物表面形貌
Fig.2. Surface morphologies of C-HRA-5 steel in supercritical water after oxidation for 200 h at 650 ℃ (a), 1000 h at 650 ℃ (b), 200 h at 700 ℃ (c) and 1000 h at 700 ℃ (d)