超超临界电站国产奥氏体钢C-HRA-5在超临界水中的氧化特性
方旭东1, 刘晓2, 徐芳泓1,3, 李瑞涛2, 朱忠亮2, 张乃强2(
)
)
Oxidation Behavior in Supercritical Water of Domestic Austenitic Steel C-HRA-5 for Uultra-supercritical Power Stations
FANG Xudong1, LIU Xiao2, XU Fanghong1,3, LI Ruitao2, ZHU Zhongliang2, ZHANG Naiqiang2()
)
图1. C-HRA-5钢在650 ℃/25 MPa和700 ℃/25 MPa超临界水中的氧化增重曲线
Fig.1. C-HRA-5 steel oxidation mass gain curves in 650 ℃, 700 ℃ and 25 MPa supercritical water