添加Zn2+对ZIRLO合金在模拟压水堆一回路含LiOH和H3BO3水溶液工况下耐腐蚀性能的影响
杨明馨(
), 高阳, 王辉
), 高阳, 王辉
Effect of Zn(CH3COO)2 Addition on Corrosion of ZIRLO Alloy in Simulated PWR Primary Loop Medium with LiOH and H3BO3
YANG Mingxin(), GAO Yang, WANG Hui
), GAO Yang, WANG Hui
图4. ZIRLO合金在360 ℃和18.6 MPa条件下不加锌和加锌的LiOH和H3BO3水溶液中腐蚀后表面氧化膜内第二相粒子的TEM明场像及EDS结果
Fig.4. TEM images (a, c) and EDS results (b, d) of the second phases in the oxide scales formed on ZIRLO alloy after corrosion at 360 ℃ under 18.6 MPa in LiOH and H3BO3 solutions without Zn2+ (a, b) and with 50 μg/kg Zn2+ (c, d)