深海压力交变加速条件下改性石墨烯有机涂层的失效机制
|
曹京宜 1, 王智峤 1, 李亮 1, 孟凡帝 2( ), 刘莉 2, 王福会 2
|
Failure Mechanism of Organic Coating with Modified Graphene Under Simulated Deep-sea Alternating Hydrostatic Pressure
|
CAO Jingyi 1, WANG Zhiqiao 1, LI Liang 1, MENG Fandi 2( ), LIU Li 2, WANG Fuhui 2
|
|
图5. 不同压力条件下石墨烯有机涂层的湿态附着力随浸泡时间的变化
|
Fig.5. Changes of wet adhesion for G and MG coatings with immersion time under alternating hydrostatic pressure
|
|
|
|
|