刘晓1, 王海2, 朱忠亮1, 李瑞涛1, 陈震宇1, 方旭东3, 徐芳泓3, 张乃强1(
)
)
Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station
LIU Xiao1, WANG Hai2, ZHU Zhongliang1, LI Ruitao1, CHEN Zhenyu1, FANG Xudong3, XU Fanghong3, ZHANG Naiqiang1()
)
图6. HR3C与Sanicro25钢在650和700 ℃超临界水中氧化不同时间后的形貌图
Fig.6. High magnification views of the square regions marked in Fig.2b (a) and Fig.3b (b), and outer (c, e, g, i) and inner (d, f, h, j) oxide scales formed on HR3C (c, d, g, h) and Sanicro25 (e, f, i, j) at 700 ℃ for 200 h (c~f) and 1000 h (g~j)