交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响
胡露露1, 赵旭阳2, 刘盼1, 吴芳芳2, 张鉴清1, 冷文华1(
), 曹发和1,3()
), 曹发和1,3()
Effect of AC Electric Field and Thickness of Electrolyte Film on Corrosion Behavior of A6082-T6 Al Alloy
HU Lulu1, ZHAO Xuyang2, LIU Pan1, WU Fangfang2, ZHANG Jianqing1, LENG Wenhua1(), CAO Fahe1,3()
), CAO Fahe1,3()
图6. 不同交流电场下铝合金在3.5%NaCl本体溶液和不同厚度薄液膜下的阴极极化曲线和-1.0 V极限扩散电流
Fig.6. Cathodic polarization curves and -1.0 V ultimate diffusion current of aluminum alloy in 3.5%NaCl bulk solution and under thin electrolyte layers with different thicknesses and AC electric fields of 0 kV/m (a, b), 20 kV/m (c, d), 60 kV/m (e, f) and 100 kV/m (g, h)