交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响
胡露露1, 赵旭阳2, 刘盼1, 吴芳芳2, 张鉴清1, 冷文华1(
), 曹发和1,3()
), 曹发和1,3()
Effect of AC Electric Field and Thickness of Electrolyte Film on Corrosion Behavior of A6082-T6 Al Alloy
HU Lulu1, ZHAO Xuyang2, LIU Pan1, WU Fangfang2, ZHANG Jianqing1, LENG Wenhua1(), CAO Fahe1,3()
), CAO Fahe1,3()
图5. 在本体3.5%NaCl溶液及不同厚度薄液膜体系中浸泡20 min后施加不同交流电场对A6082-T6铝合金开路电位的影响
Fig.5. Effects of AC electric field on the open circuit potential of A6082-T6 aluminum alloy after soaking for 20 min in 3.5%NaCl bulk solution (a) and under thin electrolyte layers with the thicknesses of 350 μm (b), 250 μm (c) and 150 μm (d)