交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响
胡露露1, 赵旭阳2, 刘盼1, 吴芳芳2, 张鉴清1, 冷文华1(
), 曹发和1,3()
), 曹发和1,3()
Effect of AC Electric Field and Thickness of Electrolyte Film on Corrosion Behavior of A6082-T6 Al Alloy
HU Lulu1, ZHAO Xuyang2, LIU Pan1, WU Fangfang2, ZHANG Jianqing1, LENG Wenhua1(), CAO Fahe1,3()
), CAO Fahe1,3()
图2. A6082-T6铝合金在本体溶液以及典型薄液膜厚度溶液中浸泡72 h的Nyquist和Bode图
Fig.2. Nyquist (a, c, e) and Bode (b, d, f) diagrams of A6082-T6 aluminum alloy immersed for 72 h in bulk solution (a, b) and under thin electrolyte layers with the thicknesses of 256 μm (c, d) and 70 μm (e, f)