海洋大气环境Cu/Ni协同作用对低合金钢耐蚀性影响
张天翼1,柳伟1(
),范玥铭1,李世民1,董宝军1,BANTHUKUL Wongpat1,CHOWWANONTHAPUNYA Thee2
),范玥铭1,李世民1,董宝军1,BANTHUKUL Wongpat1,CHOWWANONTHAPUNYA Thee2
Effect of Synergistic Action of Cu/Ni on Corrosion Resistance of Low Alloy Steel in a Simulated Tropical Marine Atmosphere
ZHANG Tianyi1,LIU Wei1(),FAN Yueming1,LI Shimin1,DONG Baojun1,BANTHUKUL Wongpat1,CHOWWANONTHAPUNYA Thee2
),FAN Yueming1,LI Shimin1,DONG Baojun1,BANTHUKUL Wongpat1,CHOWWANONTHAPUNYA Thee2
图5. 3种钢腐蚀240 h后锈层截面形貌及元素分布结果
Fig.5. Cross-sectional morphologies of 0.7Cu-0.7Ni (a), 0.4Cu-0.4N (b) and 0.3Cu-0.3Ni (c) steels after 240 h spraying test, and EDS analysis results of Cl, Cr and Cu at the marked points in Fig.5a~c (d)