应力作用下2297铝锂合金腐蚀行为研究
于美(
),魏新帝,范世洋,刘建华,李松梅,钟锦岩
),魏新帝,范世洋,刘建华,李松梅,钟锦岩
Corrosion Behavior of 2297 Al-Li Alloy under Tensile Load
YU Mei(),WEI Xindi,FAN Shiyang,LIU Jianhua,LI Songmei,ZHONG Jinyan
),WEI Xindi,FAN Shiyang,LIU Jianhua,LI Songmei,ZHONG Jinyan
图4. 不同应力作用下浸泡2 h后2297-T87铝锂合金金相显微形貌
Fig.4. Metallographic micrographs of 2297-T87 Al-Li alloy after immersion for 2 h under different stress loads: (a) 0%σ0.2， (b) 30%σ0.2， (c) 60%σ0.2， (d) 90%σ0.2， (e) 103%σ0.2