工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响
肖金涛1,陈妍1,邢明秀1,鞠鹏飞1(
),孟引根1,王芳2
),孟引根1,王芳2
Effect of Process Parameters on Corrosion Resistance of Anodizing Film on 2195 Al-Li Alloy
XIAO Jintao1,CHEN Yan1,XING Mingxiu1,JU Pengfei1(),MENG Yingen1,WANG Fang2
),MENG Yingen1,WANG Fang2
图1. 2195铝锂合金在不同浓度的硫酸溶液中阳极氧化后氧化膜的表面形貌
Fig.1. Surface morphologies of oxide films formed on 2195 Al-Li alloy after anodization in sulfuric acid solutions of 180~200 g/L (a), 230~250 g/L (b) and 270~290 g/L (c)