双级时效对7050铝合金力学性能及氢脆敏感性的影响
任建平1,宋仁国2(
)
)
Effect of Two-stage Ageing on Mechanical Properties and Sensitivity to Hydrogen Embrittlement of 7050 Aluminum Alloy
REN Jianping1,SONG Renguo2()
)
图5. 7050铝合金在743 K/70 min+393 K/8 h+423 K双级时效制度下时效不同时间的断口形貌
Fig.5. Fracture morphologies of 7050 Al alloy after ageing under the conditions of 743 K/70 min+393 K/8 h+423 K/different time: (a) 17 h (first peak); (b) 33 h (vale); (c) 45 h (second peak); (d) 57 h (after second peak)