稀土复合掺杂ZrO2陶瓷涂层抗Na2SO4+NaVO3热腐蚀性能的研究进展
陈超1,梁艳芬1,梁天权1,2(
),满泉言1,罗毅东1,张修海1,2,曾建民1,2
),满泉言1,罗毅东1,张修海1,2,曾建民1,2
Research Progress on Hot Corrosion of Rare Earth Oxides Co-doped ZrO2 Ceramic Coatings in Molten Na2SO4+NaVO3 Salts
CHEN Chao1,LIANG Yanfen1,LIANG Tianquan1,2(),MAN Quanyan1,LUO Yidong1,ZHANG Xiuhai1,2,ZENG Jianmin1,2
),MAN Quanyan1,LUO Yidong1,ZHANG Xiuhai1,2,ZENG Jianmin1,2
图5. YSZ和CYSZ在1050 ℃下Na2SO4+V2O5熔盐中分别腐蚀20和28 h后的SEM形貌[
Fig.5. SEM surface morphologies of YSZ (a) and CYSZ (b) after hot corrosion in Na2SO4+V2O5 molten salt at 1050 ℃ for 20 and 28 h, respectively[