稀土复合掺杂ZrO2陶瓷涂层抗Na2SO4+NaVO3热腐蚀性能的研究进展
陈超1,梁艳芬1,梁天权1,2(
),满泉言1,罗毅东1,张修海1,2,曾建民1,2
),满泉言1,罗毅东1,张修海1,2,曾建民1,2
Research Progress on Hot Corrosion of Rare Earth Oxides Co-doped ZrO2 Ceramic Coatings in Molten Na2SO4+NaVO3 Salts
CHEN Chao1,LIANG Yanfen1,LIANG Tianquan1,2(),MAN Quanyan1,LUO Yidong1,ZHANG Xiuhai1,2,ZENG Jianmin1,2
),MAN Quanyan1,LUO Yidong1,ZHANG Xiuhai1,2,ZENG Jianmin1,2
图2. 700和900 ℃下NaVO3腐蚀100 h后ScYSZ中m-ZrO2含量 [
Fig.2. Content of m-ZrO2 in as-prepared ScYSZ after hot corrosion in molten NaVO3 at 700 ℃ or 900 ℃ for 100 h[