基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能
夏俊捷1,牛红志2,刘敏3,曹华珍1,郑国渠1,伍廉奎1(
)
)
Enhancement of High Temperature Oxidation Resistance of Ti48Al5Nb Alloy via Anodic Anodization in NH4F Containing Ethylene Glycol
Junjie XIA1,Hongzhi NIU2,Min LIU3,Huazhen CAO1,Guoqu ZHENG1,Liankui WU1()
)
图8. 10 V电压下阳极氧化的Ti48Al5Nb合金经1000 ℃氧化100 h后的截面微观形貌及相应的EDS线扫描和面扫描结果
Fig.8. Cross-sectional SEM image of Ti48Al5Nb alloy with pre-anodizing at 10 V after oxidation at 1000 ℃ for 100 h (a), corresponding element depth profiles along the marked line (b), and distribution mappings of Al, Ti, Nb and O in the marked rectangle zone (c)