镁合金应力腐蚀开裂行为研究进展
王保杰1,栾吉瑜1,王士栋2,3,许道奎2,3(
)
)
Research Progress on Stress Corrosion Cracking Behavior of Magnesium Alloys
Baojie WANG1,Jiyu LUAN1,Shidong WANG2,3,Daokui XU2,3()
)
图1. 膜破裂-溶解导致裂纹的连续扩展和脆性区域在外力作用下发生解理开裂[
Fig.1. Continuous propagation of crack due to dissolution following film rupture (a), and cleavage-type fracture ahead of embrittled zone (b) (σ is tensile stress)[