022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究
丰涵(
),宋志刚,吴晓涵,李惠,郑文杰,朱玉亮
),宋志刚,吴晓涵,李惠,郑文杰,朱玉亮
Relationship Between Selective Corrosion Behavior and Duplex Structure of 022Cr25Ni7Mo4N Duplex Stainless Steel
Han FENG(),Zhigang SONG,Xiaohan WU,Hui LI,Wenjie ZHENG,Yuliang ZHU
),Zhigang SONG,Xiaohan WU,Hui LI,Wenjie ZHENG,Yuliang ZHU
图2. 022Cr25Ni7Mo4N双相不锈钢试样的原始两相组织以及试样在2 mol/L H2SO4+0.5 mol/L HCl混合溶液中的不同电位恒电位极化后的表面形貌
Fig.2. Original duplex structure of 022Cr25Ni7Mo4N steel (a) and surface morphologies of the sample after potentiostatic polarizations in 2 mol/L H2SO4+0.5 mol/L HCl solution at Eh potential (b) and El potential (c)