几种超级不锈钢在模拟烟气脱硫环境中的缝隙腐蚀行为研究
王长罡1,魏洁1,魏欣1,穆鑫1,薛芳1,董俊华1(
),柯伟1,李国平2
),柯伟1,李国平2
Crevice Corrosion Behavior of Several Super Stainless Steels in a Simulated Corrosive Environment of Flue Gas Desulfurization Process
Changgang WANG1,Jie WEI1,Xin WEI1,Xin MU1,Fang XUE1,Junhua DONG1(),Wei KE1,Guoping LI2
),Wei KE1,Guoping LI2
图6. 904L不锈钢人造缝隙电极在70 ℃死亡绿液中循环伏安测试后的腐蚀形貌
Fig.6. Corrosion morphology of 904L stainless steel artificial gap electrode after cyclic voltammetry in death green liquid at 70 ℃ (a) and the magnified images of the areas I (b), II (c), III (d) in Fig.6a, IV in Fig.6b (e) and V in Fig.6c (f)