Effect of Sulfuric Acid Anodizing on Mechanical Properties of 2E12 Al-alloy
Gaohong CHEN1(),Yuansen HU2,Mei YU2,Jianhua LIU2,Guoai LI1
),Yuansen HU2,Mei YU2,Jianhua LIU2,Guoai LI1
图6. 去除包铝层和带包铝层的2E12铝合金阳极氧化不同时间后的断口形貌
Fig.6. Fracture morphologies of unclad (a1~a5) and alclad (b1~b5) 2E12 Al-alloy anodized for 0 min (a1, b1), 15 min (a2, b2), 30 min (a3, b3), 45 min (a4, b4) and 60 min (a5, b5)