硫酸阳极化对2E12铝合金力学性能的影响
陈高红1(
),胡远森2,于美2,刘建华2,李国爱1
),胡远森2,于美2,刘建华2,李国爱1
Effect of Sulfuric Acid Anodizing on Mechanical Properties of 2E12 Al-alloy
Gaohong CHEN1(),Yuansen HU2,Mei YU2,Jianhua LIU2,Guoai LI1
),Yuansen HU2,Mei YU2,Jianhua LIU2,Guoai LI1
图4. 去除包铝层和保留包铝层的2E12铝合金经不同时间阳极氧化后的表面SEM像
Fig.4. Surface SEM images of unclad (a1~d1) and alclad (a2~d2) 2E12 Al-alloy after anodization for 15 min (a1, a2), 30 min (b1, b2), 45 min (c1, c2) and 60 min (d1, d2)