基于IMO标准的E36级低合金船板钢货油舱上甲板环境全周期腐蚀行为与机理*
梁金明,唐荻,武会宾(
),岳远杰
),岳远杰
Cyclic Corrosion Behavior of E36 Low-alloy Steel in a Simulated Cargo Oil Tank Upper Deck Environment Corresponding to IMO Standard
Jinming LIANG,Di TANG,Huibin WU(),Yuanjie YUE
),Yuanjie YUE
图5. 不同腐蚀周期实验钢去除腐蚀产物膜前后腐蚀形貌
Fig.5. Corrosion morphologies of test steel with different corrosion cycle before and after removing corrosion scale, (a) 21 d before removing corrosion scale, (b, c) 21 d after removing corrosion scale, (d) 49 d before removing corrosion scale, (e, f) 49 d after removing corrosion scale, (g) 77 d before removing corrosion scale, (h, i) 77 d after removing corrosion scale, (j) 98 d before removing corrosion scale, (k, l) 98 d after removing corrosion scale