THE SULPHATION AND OXIDATION CORROSION RESISTANCESTUDY OF Ni3Al-BASED ALLOY AND ITS COMPOSITES INBURNING ENVIRONMENT OF INFERIOR QUALITY COAL

J Chin Soc Corr Pro

2002, Vol. 22

Issue (2): 118-120 DOI:

Research Report

Current Issue | Archive | Adv Search

THE SULPHATION AND OXIDATION CORROSION RESISTANCESTUDY OF Ni3Al-BASED ALLOY AND ITS COMPOSITES INBURNING ENVIRONMENT OF INFERIOR QUALITY COAL

Beijing Chen;Heli Luo;Di Feng

北京钢铁研究总院高温材料所

Download:

PDF(131KB)
Export: BibTeX | EndNote (RIS)

Abstract The sulphation and oxidation corrosion resista nce of Ni3Al-based intermetallics has been investigated in this paper.In burning environment of inferior quality coal,Ni3Al-based alloy provided excellent prot ection against sulphation corrosion.Its properties of sulphation resistance is o ver 3.6 times that of 2520 heat resistant alloy,this is excellent commercial mat erial of sulphation corrosion resistance at high temperature. 

Key words: Ni3Al-based alloy sulphation corrosion resi stance WC/Ni3Al composite burning environment of inf

Received: 03 December 2001

ZTFLH:

TG172.82

Corresponding Authors: Beijing Chen

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Beijing Chen
	Heli Luo
	Di Feng

Cite this article:

Beijing Chen; Heli Luo; Di Feng. THE SULPHATION AND OXIDATION CORROSION RESISTANCESTUDY OF Ni3Al-BASED ALLOY AND ITS COMPOSITES INBURNING ENVIRONMENT OF INFERIOR QUALITY COAL. J Chin Soc Corr Pro, 2002, 22(2): 118-120 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I2/118

[1]ZhuRZ ,HeYD .TheCorrosionandCorrosionResistanceMaterialsatHighTemperature[M ].Shanghai:ShanghaiScienceandTechnol ogyPublisher,1995,200(朱日彰,何业东等.高温腐蚀及耐高温腐蚀材料[M ].上海:上海科学技术出版社,1995,200)
[2]LiRJ.Ceramics-MetalandItsComposites[M ].Beijing:Metallur gyandIndustryPublisher,1995,243(李荣久.陶瓷-金属复合材料[M ].北京:冶金工业出版社,1995,243)
[3]AndersenA ,HaflanB ,kofstadP .PropertiesofNi-Alalloy[J].Mater.Sci.Eng.,1987,87:45
[4]WagerC ,CanaveJ .CorrosionathightemperaturemechanismofNi-Alalloy[J].J .Electrochem.Soc.,1956,103:627
[5]WoottnMR ,BirksN .SulphurcorrosionofNi-basedalloy[J].Corros.Sci.,1972,12:829

[1]	YANG Mingxin, GAO Yang, WANG Hui. Effect of Zn(CH₃COO)₂ Addition on Corrosion of ZIRLO Alloy in Simulated PWR Primary Loop Medium with LiOH and H₃BO₃[J]. 中国腐蚀与防护学报, 2020, 40(2): 199-204.
[2]	Yunhai MA. Effect of Shot Peening on Oxidation Resistance of Super 304H Steel in Supercritical Steam[J]. 中国腐蚀与防护学报, 2019, 39(3): 245-252.
[3]	CHEN Dongxu, WU Xinqiang, HAN En-Hou. Research Progress of Crevice Corrosion and Crevice Corrosion Issues of Nuclear-grade Materials[J]. 中国腐蚀与防护学报, 2014, 34(4): 295-300.
[4]	LU Jintao,GU Yuefeng. High-temperature Steam Oxidation Behavior of Alloys Used for Key Parts of the Power Plant Boiler[J]. 中国腐蚀与防护学报, 2014, 34(1): 19-26.
[5]	HUANG Bensheng,YIN Wenfeng,WANG Xiaohong,SHI Yijun. Corrosion Behavior of Steels Used in Making Crude Oil Distillation Unit in High Temperature Crude Oil Fractions[J]. 中国腐蚀与防护学报, 2013, 33(5): 377-382.
[6]	PENG Dequan,HU Shilin,ZHANG Pingzhu,WANG Hui. Research on General Corrosion Property of 304L Stainless Steel in Simulated PWR Primary Water[J]. 中国腐蚀与防护学报, 2013, 33(4): 288-292.
[7]	QIAO Yanxin, REN Ai, LIU Feihua, ZHENG Yugui, TANG Rui, JIN Shuoxue, GUO Liping. EFFECT OF PROTON IRRADIATION ON CORROSION BEHAVIOR OF AUSTENITE STAINLESS STEEL AL-6XN IN HIGH TEMPRATURE HIGH PRESSURE WATER[J]. 中国腐蚀与防护学报, 2012, 32(5): 381-387.
[8]	TANG Zhanmei, HU Shilin, ZHANG Pingzhu. STRESS CORROSION CRACKING OF 316Ti IN 300℃ HIGH TEMPERATURE WATER CONTAINING CHLORIDE IONS[J]. 中国腐蚀与防护学报, 2012, 32(4): 291-295.
[9]	ZHONG Hongbin LI Meishuan ZHOU Yanchun WANG Junshan XU Zhenghui ZHANG Zhongwei. THERMODYNAMIC ANALYSIS FOR PHASE EQUILIBRIUM OF MC(B)-C-O SYSTEM IN ULTRA-HIGH TEMPERATURE CONDITIONS[J]. 中国腐蚀与防护学报, 2009, 29(4): 301-305.
[10]	FAN Liru LIU Yuwen WANG Kuan LI Yuan SUN Qina. EFFECT OF THE SAMPLE STATE ON DECHROMIZATION OF Cu-Cr ALLOY[J]. 中国腐蚀与防护学报, 2009, 29(1): 15-18.
[11]	HUANG Junbo WU Xinqiang HAN En-Hou KE Wei. PRESENT STATUS AND DEVELOPMENT ON ELECTROCHEMISTRY AT HIGH TEMPERATURES AND HIGH PRESSURES AQUEOUS SYSTEMS[J]. 中国腐蚀与防护学报, 2008, 28(6期): 374-380.
[12]	. APPLICATION OF ATOMIC FORCE MICROSCOPY IN STUDY OF SULFATE-REDUCING BACTERIA TO A3 STEEL[J]. 中国腐蚀与防护学报, 2007, 27(2): 70-.
[13]	Guanfa Lin. Effect of CO2 Partial Pressure on the Morphology of Corrosion Metallic Product Scales[J]. 中国腐蚀与防护学报, 2004, 24(5): 284-288 .
[14]	Yong Shen. High-Temperature Oxidation Resistance of High-Nb TiAl-Based Alloy[J]. 中国腐蚀与防护学报, 2004, 24(4): 203-207 .
[15]	Yuefei Zhang. High Temperature Oxidation Resistance of the Plasma Titanizing on Copper Surface by Double Glow Discharge[J]. 中国腐蚀与防护学报, 2004, 24(3): 139-142 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed