THE EFFECT OF NANOCRYSTALLIZATION ON HOT CORROSION BEHAVIOR OF K38G ALLOY AT 900℃

J Chin Soc Corr Pro

2003, Vol. 23

Issue (1): 1-6 DOI:

Research Report

Current Issue | Archive | Adv Search

THE EFFECT OF NANOCRYSTALLIZATION ON HOT CORROSION BEHAVIOR OF K38G ALLOY AT 900℃

Shujiang Geng;Shenglong Zhu;Fuhui Wang

中科院金属所;金属腐蚀与防护国家重点实验室

Download:

PDF(318KB)
Export: BibTeX | EndNote (RIS)

Abstract The sputtered nanocrystalline coating of K38G alloy was obtained by magnetron sputtering.The effect of nanocrystallization on the h ot corrosion behavior of K38G alloy at 900℃ was studied.The results indicated t hat the internal sulfidation was eliminated for the coating by pre-deposition wi th 0.8 mg/cm2 of 75%Na2SO4+25%K2SO4.Although the internal sulfides wer e still formed for the coating by pre-deposition with 3 mg/cm2 of 75%Na2SO 4+25%K2SO4,the hot corrosion resistance of K38G alloy was clearly enhanced t hrough nanocrystallization.The hot corrosion mechanism was proposed.

Key words: K38G sputtered nanocrystalline coating hot corrosion

Received: 13 July 2001

ZTFLH:

TG174.4

Corresponding Authors: Shujiang Geng

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Shujiang Geng
	Shenglong Zhu
	Fuhui Wang

Cite this article:

Shujiang Geng; Shenglong Zhu; Fuhui Wang. THE EFFECT OF NANOCRYSTALLIZATION ON HOT CORROSION BEHAVIOR OF K38G ALLOY AT 900℃. J Chin Soc Corr Pro, 2003, 23(1): 1-6 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I1/1

[1]WangF ,LouH ,BaiL .MagnetronsputteredCoCrAlYcoatingsonsuperalloyIN738[J].Chin.J .Met.Sci.Tech.,1990,6:61
[2]LouH ,WangF ,XiaB ,ZhangL .High-temperatureoxidationre sistanceofsputteredmicro-grainsuperalloyK38G [J].Oxid.Met.,1992,38:299
[3]LouH ,WangF ,ZhuS ,XiaB ,ZhangL .OxideformationofK38Gsuperalloyanditssputteredmicrograinedcoating[J].Surf.Coat.Tech.,1994,63:105
[4]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3scales[J].Oxid.Met.,1997,48:215
[5]WangF ,YoungDJ .EffectofnanocrystallizationonthecorrosionresistanceofK38GsuperalloyinCO +CO2 atmospheres[J].Oxid.Met.,1997,48:497
[6]GoebelJA ,PettitFS .Na2SO4-inducedacceleratedoxidation(hotcorrosion)ofnickel[J].Metall.Trans.,1970,1:1943
[7]GoebelJA ,PettitFS ,GowardGW .Mechanismsforthehotcor rosionofnickel-basealloys[J].Metall.Trans.,1973,4:261
[8]ZhangYS .SolubilityofCr2O3infusedNa2SO4at1200K[J].J .Electrochem.Soc.,1986,133:655
[9]WangMC ,JinZJ,etal.Structureandhot-corrosionresistancepropertiesofM 38superalloyinlaser-irradiatedzones[J].J .Chi neseSocietyforCorrosionandProtection,1986,6:65(王茂才,金柱京等.M 38合金激光辐照层的结构及其抗热腐蚀性能[J].中国腐蚀与防护学报,1986,6:65)
[10]ZhangY .DissolutionbehaviorofmetaloxidesinfusedNa2SO4[J].J .ChineseSocietyCorrosionandProtection,1989,9:121(张允书.金属氧化物在熔融Na2SO4中的溶解行为[J].中国腐蚀与防护学报,1989,9:121)

[1]	CHEN Chao,LIANG Yanfen,LIANG Tianquan,MAN Quanyan,LUO Yidong,ZHANG Xiuhai,ZENG Jianmin. Research Progress on Hot Corrosion of Rare Earth Oxides Co-doped ZrO₂ Ceramic Coatings in Molten Na₂SO₄+NaVO₃ Salts[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[2]	Lijia YU,Wenping LIANG,Hao LIN,Qiang MIAO,Biaozi HUANG,Shiyu CUI. Evaluation of Hot Corrosion Behavior of Laser As-remelted YSZ Thermal Barrier Coatings at 950 ℃[J]. 中国腐蚀与防护学报, 2019, 39(1): 77-82.
[3]	Hao CHEN,Qing CHEN,Li XIN,Long SHI,Shenglong ZHU,Fuhui WANG. Preparation and High Temperature Corrosion Behavior of Aluminized Nanocrystalline Coating on DD98M Alloy[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
[4]	Xijing WANG, Boshi WANG, Chao YANG, Yan YANG, Bin SHEN. Hot Corrosion of Pure Nickel and Its Weld Joints in Molten Na₂SO₄-K₂SO₄ Salts[J]. 中国腐蚀与防护学报, 2018, 38(5): 495-501.
[5]	Xizhong WANG,Jianhao WU,Hui PENG,Hongbo GUO,Shengkai GONG. Hot-gas Corrosion Resistance of La₂Ce₂O₇/8YSZ Duble-ceramic-layered Thermal Barrier Coating[J]. 中国腐蚀与防护学报, 2017, 37(1): 36-40.
[6]	Guangming LIU,Kangsheng LIU,Xiaofei MAO,Zhongping WAN,Jianhang HUANG,Mingming YU,Yuankui WANG. Hot Corrosion of T91 Steel in Molten Mixture of KCl+Na₂SO₄+K₂SO₄[J]. 中国腐蚀与防护学报, 2017, 37(1): 23-28.
[7]	Bo YANG,Maodong LI,Guangming LIU,Yuankui WANG,Kangsheng LIU,Wei ZHAI,Jianhang HUANG. Hot Corrosion Behavior of Inconel 625/NiCr Coating Prepared by HOVF[J]. 中国腐蚀与防护学报, 2016, 36(5): 483-488.
[8]	WU Duoli, ZHANG Hongyu, WEI Hua, ZHENG Qi, JIN Tao, SUN Xiaofeng. Hot Corrosion Behavior of Four Modified Aluminide Coatings on DZ38G Alloy[J]. 中国腐蚀与防护学报, 2014, 34(6): 502-506.
[9]	WANG Li，LIU Chunyang，HAN Zhenyu, TONG Wenwei. HOT CORROSION BEHAVIOR AND EVALUATION OF TURBINE COMPONENTS AND MATERIALS USED FOR GAS TURBINE ENGINE[J]. 中国腐蚀与防护学报, 2011, 31(5): 399-403.
[10]	XU Yangtao, XIA Tiandong, YAN Jianqiang. EFFECT OF ALLOYING ELEMENTS TO HOT CORROSION BEHAVIOR OF NOVEL Co-Al-W SUPERALLOY[J]. 中国腐蚀与防护学报, 2010, 30(6): 457-464.
[11]	WEI Hua; HUANG Liang; LIANG Jingjing; SUN Xiaofeng; GUAN Hengrong; HU Zhuangqi. EFFECT OF Re ON THE HOT-CORROSION BEHAVIOR OF A NiCrAlY OVERLAY COATING[J]. 中国腐蚀与防护学报, 2010, 30(2): 150-154.
[12]	ZHU Ming LI Meishuan ZHOU Yanchun. HOT CORROSION RESISTANCE OF Cr_1-xAl_xN COATINGS ON A Ti₃Al BASED ALLOY IN DEPOSITED (Na₂SO₄+K₂SO₄) MOLTEN SALT AT 800 ℃[J]. 中国腐蚀与防护学报, 2009, 29(4): 306-311.
[13]	;. STUDY OF HOT CORROSION RESISTANCES OF TWO NICKEL BASE SUPERALLOYS FOR DIRECTIONAL SOLIDIFICATION[J]. 中国腐蚀与防护学报, 2008, 28(5): 277-281 .
[14]	. High Temperature Oxidation and Hot Corrosion Behavior of Enamel/Sputtered NiCrAlY Composite Coating[J]. 中国腐蚀与防护学报, 2005, 25(6): 344-350 .
[15]	Yun LI; Jianting Guo; Chao YUAN; Hongcai YANG; Long FANG; Xuegui LIU. HOT CORROSION OF NICKEL-BASE CAST SUPERALLOY K35 AT 800℃[J]. 中国腐蚀与防护学报, 2005, 25(4): 250-255 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed