Characteristics of Tungsten Alloy Layer Formed at Different Temperatures by Double Glow Plasma Surface Alloying
Hong Zhang;;
太原理工大学 表面工程研究所
Download:  PDF(218KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The formation of tungsten alloy layer on carbon steel by double glow plasma surface alloying has been studied by means of SEM、XRD and other measurements. The surface layer so produced could he divided into three parts: deposition layer, diffusion layer and matrix. The study results showed that the deposition layer was constituted by W with body-centred cubic lattice and preferred orientation. The phase in the diffusion layer was α-Fe solid solution containing W and some carbide FeW3C was found in it. The matrix was T8 carbon steel. With the increase in deposition temperature, the microstructure of the deposition layer changed from the tapered outgrowth to the columnar form. It resulted in the increase of its corrosion-resistance, however, its wear resistance decreased.
Key words:  tungsten deposition layer      glow discharge      plasma surface alloying      
Received:  06 January 1999     
ZTFLH:  TG172.445  
Corresponding Authors:  Hong Zhang   

Cite this article: 

Hong Zhang. Characteristics of Tungsten Alloy Layer Formed at Different Temperatures by Double Glow Plasma Surface Alloying. J Chin Soc Corr Pro, 2000, 20(1): 59-63 .

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y2000/V20/I1/59

[1]XuZ .Methodandapparatusforintroducingnormallysolidmaterialsintosubstratesurfaces [P] USPatent:No .4 52 0 2 6 8
[2 ]MovchanBA ,DemchisinAV .Structureandpropertiesofthicknickel,titanium ,tungsten ,aluminiumoxideandzirco niumdioxidevacuum depositedfilms.FizikaMetalloriMetallovelenie,196 9,2 8(4 ) :6 53- 6 6 0 .
[3]ThorntonJA .Themicrostructureofsputter-depositedcoatings[J] JVacSciTech ,1986 ,A4 :30 59
[4 ]王福贞 .表面沉积技术 [M] 北京 :机械工业出版社 ,1989.P12 3
[1] SHI Kunyu,ZHANG Jinzhong,ZHANG Yi,WAN Yi. Preparation and Corrosion Resistance of Nb2N Coating on TC4 Ti-alloy[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[2] Zhiyong He. STUDY ON ABSORPTION RATIO OF ALLOY ELEMENTS IN PLASMA Ni-Cr ALLOYING BY DOUBLE GLOW PLASMA PROCESS[J]. 中国腐蚀与防护学报, 1999, 19(6): 345-350 .
[3] LI Zhong-hou LIU Xiao-ping SU Yong-an XU Zhong (Taiyuan University of Technology; Taiyuan 030024). DIFFUSION OF PENETRATED ATOMS IN MATRIX DURING DOUBLE GLOW PLASMA SURFACE ALLOYING[J]. 中国腐蚀与防护学报, 1998, 18(1): 77-80.
[4] GAO Yuan HE Zhiyong XU Chong (Taiyuan University of Technology; Taiyuan 030024). PASTE PLASMA ALUMINIZING BY HOLLOW CATHODE DISCHARGE[J]. 中国腐蚀与防护学报, 1997, 17(4): 286-290.
No Suggested Reading articles found!