STUDY ON DESTROY PROCESS OF 1Cr18Ni9Ti STAINLESS STEEL SURFACE PASSIVE FILM BY HYDROGEN SULFIDE

J Chin Soc Corr Pro

2002, Vol. 22

Issue (1): 22-26 DOI:

Research Report

Current Issue | Archive | Adv Search

STUDY ON DESTROY PROCESS OF 1Cr18Ni9Ti STAINLESS STEEL SURFACE PASSIVE FILM BY HYDROGEN SULFIDE

Liewei Liu;Qian Hu;Feng Guo

武汉华中科技大学化学系

Download:

PDF(138KB)
Export: BibTeX | EndNote (RIS)

Abstract The behavior of 1Cr18Ni9Ti stainless steel surface passive film have been studied by potentiodynamic、impendance and electron probe in 0.05 mol/L H2SO4 solution containing hydrogen sulfide.The results indica ted that the thickness of passive film attenuated with the increasing content of hydrogen sulfide,but the film did not destroy at a low concentration of hydroge n sulfide,the EIS characteristic of passive film remained.The passive film destr oyed at a high concentration of hydrogen sulfide (>200×10-6),and the surf ace film turned to sulfide film,then EIS characteristic changed as a result.

Key words: surface film impendance hydrogen sulfide corrosion

Received: 21 September 2000

ZTFLH:

TG172

Corresponding Authors: Liewei Liu

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Liewei Liu
	Qian Hu
	Feng Guo

Cite this article:

Liewei Liu; Qian Hu; Feng Guo. STUDY ON DESTROY PROCESS OF 1Cr18Ni9Ti STAINLESS STEEL SURFACE PASSIVE FILM BY HYDROGEN SULFIDE. J Chin Soc Corr Pro, 2002, 22(1): 22-26 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I1/22

[1]YanLJ,DongJH ,NiuL .Studyoncorrosionmechanismofironinsulfuricacidsolutionscontaininghydrogensulfide[J].J.ofChineseSocietyforCorrosionandProtection,1998,18(4):270-275
(闫丽静,董俊华,牛林等.铁在含H2S的硫酸溶液中的腐蚀机制研究[J].中国腐蚀与防护学报,1998,18(4):270-275)
[2]VedageH ,RamanarayananTA ,MumfordJD ,SmithSN .Electro chemicalgrowthofironsulfidefilmsinH2S -saturatedchlorideme dia[J].Corrosion,1993,49(2):114-121
[3]ZhangXY ,DuYL .Effectofironsulfidescaleoncorrosionbehav iorofUNSG11180steelin5%NaClsolutioncontainingH2S [J].CorrosionScienceandProtectionTechnology,1997,9(1):19-22
(张学元,杜元龙.Fe的硫化物膜对UNSG11180钢在含H2S的NaCl溶液中的腐蚀行为影响[J].腐蚀科学与防护技术,1997,9(1):19-22)
[4]ChineseNationalPetroleumCorporation.Mensurationofhydrogensulfidecontentsinnaturalgas,iodinequantitymethod[S].NationalStandardofChina.GB ,110601-89
(中国石油天然气总公司.天然气中H2S含量的测定,碘量法[S].中华人民共和国国家标准,GB ,110601-89)
[5]SongGL ,CaoCN ,LinHC .GeneralcircuitforEISofanirreversibleelectrodeunderelectrochemicalstepcontrolandparametersanalysisofthecircuit[J].J.ofChineseSocietyforCorrosionandProtection,1994,14(2):113-122
(宋光铃,曹楚南,林海潮.电化学控制条件下不可逆电极过程交流阻抗统一换算电路和电化学参数解析[J].中国腐蚀与防护学报,1994,14(2):113-122)
[6]CaoCN .Ontheequivalentcircuitsoffaradaicimpedanceofirre versibleelectrodereactions[J].J .ofChineseSocietyforCorrosionandProtection,1990,10(2):159-170
(曹楚南.论不可逆电极法拉第阻抗等效电路类型[J].中国腐蚀与防护学报,1990,10(2):159-170)

[1]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[3]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[4]	HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[5]	ZHANG Yuxuan, CHEN Cuiying, LIU Hongwei, LI Weihua. Research Progress on Mildew Induced Corrosion of Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[6]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[7]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[8]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[10]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[11]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[12]	ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[13]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[14]	YU Hongfei, SHAO Bo, ZHANG Yue, YANG Yange. Preparation and Properties of Zr-based Conversion Coating on 2A12 Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[15]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed