THE EFFECT OF ADDITION OF NO_3~- OR NO_2~- IN Cl~- CONTAINING SOLUTION ON CHEMICAL CONDITION WITHIN CRACKS OF AUSTENITIC STAINLESS STEEL

J Chin Soc Corr Pro

1988, Vol. 8

Issue (2): 96-104 DOI:

Current Issue | Archive | Adv Search

THE EFFECT OF ADDITION OF NO_3~- OR NO_2~- IN Cl~- CONTAINING SOLUTION ON CHEMICAL CONDITION WITHIN CRACKS OF AUSTENITIC STAINLESS STEEL

Zuo Jingyi Jin Zhiqiang (Beijing Institute of chemical Technology)

Download:

PDF(758KB)
Export: BibTeX | EndNote (RIS)

Abstract A simulated occluded cell was used to study the changes within crevices or cracks of Cr18Ni9 austenitic stainless steel in Cl~-+NO_3~-(or NO_2~-)solution. It was found that in the occluded cell pH dropped more slowly than in plain Cl~- solution and approached a limiting value at about2. The ratio of migration rate of Cl~- to NO_3~- in g-eq. was approximately the same as that of the concentrations of Cl-/NO_3~- in original solution. When 1F quantity of electricity passed, about 0.5～0.7 g-eq. of Cl~-+NO_3~- migrated into the occlude cell. Migration of NO_2~- was negligible. Addition of sufficient NO_3~- or NO_2~- also caused critical potential to move in the more positive direction and the crack tip s into the passive state.

Received: 25 April 1988

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

Zuo Jingyi Jin Zhiqiang (Beijing Institute of chemical Technology). THE EFFECT OF ADDITION OF NO_3~- OR NO_2~- IN Cl~- CONTAINING SOLUTION ON CHEMICAL CONDITION WITHIN CRACKS OF AUSTENITIC STAINLESS STEEL. J Chin Soc Corr Pro, 1988, 8(2): 96-104.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1988/V8/I2/96

[1] Pourbaix, M.; the Theory of Stress Corrosion Cracking in Alloys, ed. J. C. Scully, P. 17～63(1971)
[2] Fontana,M.G.;Greene,N.D.,腐蚀工程,左景伊泽,化学工业出版社,P.39～41(1982) .
[3] Rosenfeld, I. L.; Marshakov, I. K., Corrosion, 20, 115 t(1964)
[4] 左景伊,金志强,化工学报,No.4,291～301(1982)
[5] Uhlig, H. H.; Cook,E. W., J. Electrochem. Soc., 116, 175(1967)
[6] 左景伊,应力腐蚀破裂,西安交通大学出版社,P.14,123(1985)
[7] 左景伊,金志强,孙汝宏,徐玉宝,冯兴奎,在蚀孔、缝隙或应力腐蚀裂缝中的闭塞电池腐蚀的加速效应和临界pH值,参加第十届国际金属腐蚀会议论文(Madras,Nov.1987)
[8] 左景伊,金志强,赵舂英,1Cr18Ni9Tr奥氏体不锈钢在含Cl~-+NO_3~-模拟闭塞区溶液中的腐蚀行为(待发表),(1986)

No related articles found!

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed