THE RETARDATION OF INCIPIENT STRESS CORROSION CRACK CROWTH IN SMOOTH SPECIMENS UNDER LOW FRE QUENCY CYCLIC LOADING

J Chin Soc Corr Pro

1988, Vol. 8

Issue (3): 182-188 DOI:

Current Issue | Archive | Adv Search

THE RETARDATION OF INCIPIENT STRESS CORROSION CRACK CROWTH IN SMOOTH SPECIMENS UNDER LOW FRE QUENCY CYCLIC LOADING

Yu Jjan(Shanghai Research Institute of Materials; China) R. N. Parkins(The University of Newcastle upon Tyne; U. K.)

Download:

PDF(1613KB)
Export: BibTeX | EndNote (RIS)

Abstract Smooth specimens of 70/30 brass exposed to 1N NaNO_2 aqueous solution were used to investigate the retardation of incipient stress corrosion crack growth under low frequency cyclic loading (LFCL), a phenomenon previously observed in smooth specimens of mild steel when tested in carbonate/bicarbonate solutions. It is shown that retardation was more pronounced in fine grained brass than in coarse grained brass. Additionally, a greater number of cracks formed at grain boundaries or twin boundaries in the fine grained than in the coarse grained material. The retardation effect on crack growth could be eliminated by the introduction of a pre-crack prior to testing. The results have been interpreted in terms of multiple crack initiations at smooth surfaces which effectively dispersed the strain concentration at crack tips in the incipient growth stage.

Received: 25 June 1988

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

Yu Jjan(Shanghai Research Institute of Materials; China) R. N. Parkins(The University of Newcastle upon Tyne; U. K.). THE RETARDATION OF INCIPIENT STRESS CORROSION CRACK CROWTH IN SMOOTH SPECIMENS UNDER LOW FRE QUENCY CYCLIC LOADING. J Chin Soc Corr Pro, 1988, 8(3): 182-188.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1988/V8/I3/182

[1] Parkins,R.N.,英国纽卡斯尔大学冶金及工程材料系内部实验报告,(1983)
[2] Parkins, R. N., Brit. Corr. Jnl., Ⅰ(1) , 15(1972)
[3] Yu Jian(俞健); PhD. Thesis, The Univsity of Newcastle upon Tyne(1984)
[4] Parkins, R. N.; Slattery, P. W.; Poulson, B. S., Corrosion, 37 (11) , 650 (1981)
[5] Sutcliffe, J. M.; Fesslcr, R. R.; Boyd, W. K.; Parkins, R. N.; Corrosion,28, 313 (1972)
[6] Yu Jian (俞健); Parkins, R. N.; Xu Yuan (徐源); Thompson, G.; Wood, G. C., Corros. Sci., 27(2) . 141(1987)
[7] Yu Jian (俞健), Holroyd, N. J. Henry; Parkins, R. N., Environment-Sensitive Fracture: Evaluation and Comparison of Test Methods, ASTM STP 821, Dean, S. W.; Pugh, E. N.; Ugiansky, G. M.; Eds., ASTM, Philadelphia, 288 (1984)
[8] Yu Jian(俞健); Parkins, R. N., Corros. Sci., 27(2) , 159(1987)
[9] Alvarez, M. G.; Manfredi, C.; Giordano, M.; Galvelc, J. R., Corros. Sci.,24, 769 (1984)
[10] 俞健,腐蚀与防护,2,2(1986)
[11] Lahiri, A. K.; Nayak, S. P., Corros. Sci., 11(6) , 84(1971)
[12] Congleton, J.; Shoji, T.; Parkins, R. N.; Corrosion Sci, 25(8/9) , 633 (1985)
[13] Congleton, J., 即将发表

No related articles found!

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed