| XPS, FT-IR AND RAMAN SPECTRUM STUDIES OF ATMP-Fe COORDINATION COMPOUND FILM |
| Fang Jinli~1; Li Ying~2; Ye Xiangrong~1 and Wang Zhanwen~2 1(Nanjing University) 2(Nanjing Institute of Chemical Technology) |
|
|
|
|
Abstract The protective surface film formed of carbon steel after a treatment in 1.0 mol/L amino-trimethylidenephosphonic acid(ATMP) solution was analysed by XPS, FT-IR and Raman spectrometer. The restlts showed that an anticorrosive coordination compound film was formed on the steel surface. By Ar~+ sputtering, the composition depth profile of the film was determind. The relative atomic percent contents(A. C. ％) of the film, as obtained from the element composition constant region of the profile curves, were 48.4％O; 28.6％P; 7.0％Fe; 4.3％N; 11.7％C. The structure of the coordination compound film was deducted from the above results, as probably [Fe(ATMP)_2]_n.
|
|
Received: 25 August 1992
|
Cite this article:
Fang Jinli~1; Li Ying~2; Ye Xiangrong~1 and Wang Zhanwen~2 1(Nanjing University) 2(Nanjing Institute of Chemical Technology). XPS, FT-IR AND RAMAN SPECTRUM STUDIES OF ATMP-Fe COORDINATION COMPOUND FILM. J Chin Soc Corr Pro, 1992, 12(4): 308-314.
URL:
https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1992/V12/I4/308
|
[1] Michel.D.,Corrosion,37(5) .262(1989)
[2] Eur.Plat..1O.485
[3] U.S,Pat.4． 276． 089． 4,409,121,4,717,541
[4] 方景礼,石油化工.(7) .422(1980)
[5] Fang Jingli.Wu Naijun.Wang zhanwen.Li Ying,Corrosion,47(3) ,169(1991) ;应用化学.7(2) .9(1990)
[6] Fang Jingli.Cai zi,Plat.&.Surf.Finist..77(2) ,58(1988)
[7] Fang Jingli.Wu Naijun.Plat.&.Surf.Finist.,77(2) ,54(1990)
[8] 方景礼,李莹,叶向荣,王占文,表面技术,(4) ,12(1991)
[9] F.R.G.Standard Din 50,942(1970)
[10] Weber.J.Prace Inst.Mech.Precyz.,l6． 19(1956)
[11] B..A.A.,19,2119(1988)
[12] Carter.R.P.,Inorg.Chem.,6． 393(1967)
[13] Smith.T.D.J.,Inorg.Nucl.Chem.,9,150(1959)
[14] Moedritzer.K..Syn.Inorg.Metal-org.Chem.,2(4) ,137(1972)
[15] Goggjn.P.L..Woodwand.L.A.,Trans Faraday Soc.58,1495(1962) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|