J Chin Soc Corr Pro  1995, Vol. 15 Issue (2): 135-140    DOI:
Current Issue | Archive | Adv Search |
HIGH TEMPERATURE OXIDATION AND HOT CORROSION BEHAVIOUR OF NiAl-20at% Fe ALLOY
Wang Shuhe; Guo Jianting;Lai Wanhui;Tan Minghui;Li Hui;Sun Chao(Institute of Metal Research; Chinese Academy of Sciences)
Download:  PDF(1253KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The oxidation and hot corrosion of NiAl-20Fe alloy at 850~1150℃ and 850~950℃ respectivelywere studied. It was shown that both oxidation and hot corrosion of the alloy obey the parabolic ratelaw. The addition of 20at% Fe to intermetallic compound NiAl caused a little drop in oxidation resistance,but a great decrease in resistance against hot corrosion. Compared with NiAl-30Fe, due to a decrease inFe content, an increase in Al content and the addition of Y and Ce, the NiAl-20Fe alloy showed someimprovements in oxidation resistance but little benefit in hot corrosion performance.
Received:  25 April 1995     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

Wang Shuhe; Guo Jianting;Lai Wanhui;Tan Minghui;Li Hui;Sun Chao(Institute of Metal Research; Chinese Academy of Sciences). HIGH TEMPERATURE OXIDATION AND HOT CORROSION BEHAVIOUR OF NiAl-20at% Fe ALLOY. J Chin Soc Corr Pro, 1995, 15(2): 135-140.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1995/V15/I2/135

VedulaK,PathaveV,AslanidisI,TitranRH.MatResSoc.Symp.Proc,1985;39:4112VedulaK,StephensJR.Mat.Res.Soc.Symp.Proc,1987,81:3813王淑荷,宇航材料工艺,1993;23(2):14RudyM,SanthoffG.Mat、Res.Soc.Symp.Proc.;1985,39:3275GuhaSumit,MunroePaulR,BakerIan.Mat.Res.Soc.Symp.Proc,1989,133:6336DaroliaRan,JOMJournaloftheMinerals,Metals&MaterialsSociety1991,43(3):447王淑荷,郭建亭,赖万慧,谭明晖,李辉,孙超,中国腐蚀与防护学报,1993,13(4):3578SequeiraCAC,HuckingMG.Corrosion;1981,37:3929MasahircKA,KazuhiroSG,RobertAR.Thans.ISIJ1980,20:646
No related articles found!
No Suggested Reading articles found!