ELECTROCHEMICAL CORROSION BEHAVIOR OF Ni_3 Al(B)-BASED INTERMETALLIC COMPOUNDS INLi_2CO_3-K_2CO_3 MOLTEN SALT
Xu Songbo;Chen Junming(Shanghai Institute of Metallurgy; Chinese Academy of Sciences)
Download:  PDF(508KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The electrochemical corrosion behavior of three intermotallic compounds,i.e.Ni3Al(B),Ni3Al(B)CrZr and Ni3Al(B)-Cr-Mg-RE,in 62 Li2CO3-38K2CO3(mol%)molten salt was studied.It was found thatthe anodic polarization curves of three Ni3Al(B) baSed alloys showed characteristiCS of active -passivetranspaseive stages, while two dual-phase Ni3Al(B)-Cr blloys exhibited an additional prepassiverange,similar to pure nickel, due to the contribution of Ni(M)phase.The potential range of passive statefor the alloys under study was-220~+240 mV(vs.Ag/AgCl).Based on the results of XRD and AES,thedissolution-oxide formation process at various potential stages was discussed respectively.
Key words:  Anodic polarization curve t Ni3Al(B)intermetallic compounds      Li2CO3-K2CO3 moltensalt     
Received:  25 June 1995     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

Xu Songbo;Chen Junming(Shanghai Institute of Metallurgy; Chinese Academy of Sciences). ELECTROCHEMICAL CORROSION BEHAVIOR OF Ni_3 Al(B)-BASED INTERMETALLIC COMPOUNDS INLi_2CO_3-K_2CO_3 MOLTEN SALT. J Chin Soc Corr Pro, 1995, 15(3): 161-166.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1995/V15/I3/161

1StoloffNS.Inter.Mater.Rev.,1989;34(3):153-1832徐颂波,陈俊明.金属学报,1994,30(5):A2213NatesonK.In:StoloffNS,KochCC,LiuCT,lzumiOed.Hightemperatureorderedintermetallicalloys,Mater.Res.Soc.Symp.Proc,1987.81:459-4664KuenzlyJD,DouglassDL.Oxide.Met.,1974,8:1395AtsushiNishikata.Mater.Sci.Eng,1991,A146:15-316ApplebyAJ,NicholosonSB.J.Electroana.Chem.,1974.53:105-1197ApplebyAJ,NicholosonSB.JElectroana.Chem.,1977,83:309-3288ApplebyAJ,NicholosonSB.J.Electroana.Chem.,1980;112:71-76
No related articles found!
No Suggested Reading articles found!