Corrosion Behavior of Typical Grounding Materials in Artificial Alkaline Soil Solution |
GAO Zhiyue(), JIANG Bo, FAN Zhibin, WANG Xiaoming, LI Xingeng, ZHANG Zhenyue |
State Grid Shandong Electric Power Research Institute, Ji'nan 250001, China |
|
|
Abstract The corrosion behavior of three metal materials (Q235 steel, galvanized steel and pure copper) in an artificial solution, aiming to simulate the typical alkaline soil solution of Shandong province, was studied by means of electrochemical testing technique, optical metallographic microscope and laser confocal microscope (CLSM). The results show that the corrosion degree of the three metal materials is varied in the simulated alkaline soil solution. The anodic processes of them are all metal dissolution, while the cathodic processes are all oxygen absorption reaction. The corrosion resistance of Q235 steel is the worst. Q235 steel and galvanized steel show the characteristics of uniform corrosion. Pitting occurs on the surface of pure copper. Generally, the corrosion resistance of the three metals may be ranked as follows: pure copper>galvanized steel>Q235 steel.
|
Received: 07 March 2022
32134.14.1005.4537.2022.061
|
|
Fund: Science and Technology Project of State Grid Shandong Electric Power Company(52062620004K) |
1 |
Tian P H, Tan B, Tong X F, et al. Accelerated corrosion performance comparison of several new grounding materials [J]. Corros. Prot., 2021, 42: 63
|
|
田鹏辉, 谭波, 童雪芳 等. 几种新型接地材料的加速腐蚀性能对比 [J]. 腐蚀与防护, 2021, 42: 63
|
2 |
Su Y G, Fang B L, Lv P H, et al. Initial corrosion behavior of grounding materials in three typical soils in shaanxi province [J]. Corros. Sci. Prot. Technol., 2018, 30: 279
|
|
苏耀国, 房本岭, 吕平海 等. 接地材料在陕西典型土壤中的初期腐蚀行为 [J]. 腐蚀科学与防护技术, 2018, 30: 279
|
3 |
Zhu Y C, Liu G M, Liu X, et al. Investigation on interrelation of field corrosion test and accelerated corrosion test of grounding materials in red soil environment [J]. J. Chin. Soc. Corros. Prot., 2019, 39: 550
|
|
朱亦晨, 刘光明, 刘欣 等. 红壤地区接地材料现场埋样与加速腐蚀实验的相关性研究 [J]. 中国腐蚀与防护学报, 2019, 39: 550
|
4 |
Ding C, Zhang J L, Yu Y C, et al. Corrosion kinetics of A572Gr.65 steel in different simulated soil solutions [J]. J. Chin. Soc. Corros. Prot., 2022, 42: 149
|
|
丁聪, 张金玲, 于彦冲 等. A572Gr.65钢在不同土壤模拟液中的腐蚀动力学 [J]. 中国腐蚀与防护学报, 2022, 42: 149
|
5 |
Yu D Y, Liu Z Y, Du C W, et al. Research progress and prospect of stress corrosion cracking of pipeline steel in soil environments [J]. J. Chin. Soc. Corros. Prot., 2021, 41: 737
|
|
余德远, 刘智勇, 杜翠薇 等. 管线钢土壤应力腐蚀开裂研究进展及展望 [J]. 中国腐蚀与防护学报, 2021, 41: 737
|
6 |
Wang X H, Yang Y, Chen Y C, et al. Effect of alternating current on corrosion behavior of X100 pipeline steel in a simulated solution for soil medium at korla district [J]. J. Chin. Soc. Corros. Prot., 2020, 40: 259
|
|
王新华, 杨永, 陈迎春 等. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响 [J]. 中国腐蚀与防护学报, 2020, 40: 259
|
7 |
Zhao B Z, Zhu M, Yuan Y F, et al. Comparison of corrosion resistance of CoCrFeMnNi high entropy alloys with pipeline steels in an artificial alkaline soil solution [J]. J. Chin. Soc. Corros. Prot., 2022, 42: 425
|
|
赵宝珠, 朱敏, 袁永锋 等. CoCrFeMnNi高熵合金和管线钢在碱性土壤环境中的耐蚀性对比研究 [J]. 中国腐蚀与防护学报, 2022, 42: 425
|
8 |
Yan F J, Li X G, Jiang B, et al. Corrosion behavior of pure copper in alkaline soil [J]. Corros. Sci. Prot. Technol., 2019, 31: 155
|
|
闫风洁, 李辛庚, 姜波 等. 纯铜在碱性土壤中的腐蚀行为 [J]. 腐蚀科学与防护技术, 2019, 31: 155
|
9 |
Chen K F, Zhang Z D, Hu J Y, et al. Research on corrosion behavior of four kinds of metal grounding materials in soil leaching solution [J]. Mater. Prot., 2018, 51(12): 12
|
|
陈科锋, 张兆德, 胡家元 等. 4种接地金属材料在土壤浸出液中的腐蚀行为研究 [J]. 材料保护, 2018, 51(12): 12
|
10 |
Zhu Y C, Liu G M, Wang J J, et al. Electrochemical corrosion behaviors of typical grounding materials in water-saturated acid red soil [J]. Mater. Mech. Eng., 2020, 44(9): 36
|
|
朱亦晨, 刘光明, 王金金 等. 典型接地材料在水饱和酸性红壤中的电化学腐蚀行为 [J]. 机械工程材料, 2020, 44(9): 36
|
11 |
Yu J F, Zhan Y Z. Electrochemical impedance spectroscopy (EIS) of Q235 steel in acidic soil [J]. Hubei Electr. Power, 2010, 34(6): 25
|
|
余建飞, 詹约章. Q235钢在酸性土壤中的电化学阻抗谱特征 [J]. 湖北电力, 2010, 34(6): 25
|
12 |
Yu J F, Zhou X J, Zhang Y, et al. Corrosion behavior of sherardizing steel in different soils at four typical test sites [J]. Corros. Sci. Prot. Technol., 2019, 31: 128
|
|
余建飞, 周学杰, 张予 等. 渗锌钢在4种典型土壤环境中的腐蚀行为 [J]. 腐蚀科学与防护技术, 2019, 31: 128
|
13 |
Zhu M, Du C W, Li X G, et al. Corrosion behavior of Q235 steel in beijing soil environment [J]. J. Chin. Soc. Corros. Prot., 2013, 33: 199
|
|
朱敏, 杜翠薇, 李晓刚 等. Q235钢在北京土壤环境中的腐蚀行为 [J]. 中国腐蚀与防护学报, 2013, 33: 199
|
14 |
Tang R M, Zhu Y C, Liu G M, et al. Gray correlative degree analysis of Q235 steel/conductive concrete corrosion in three typical soil environments [J]. J. Chin. Soc. Corros. Prot., 2021, 41: 110
|
|
唐荣茂, 朱亦晨, 刘光明 等. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析 [J]. 中国腐蚀与防护学报, 2021, 41: 110
|
15 |
Chen W, Jiao X Y, Zhao Z Q, et al. Corrosion behavior of hot-dip zinc-coated steel in soil environment of Northern China [J]. Electroplat. Finish., 2021, 40: 1646
|
|
陈威, 焦小雨, 赵自强 等. 热镀锌钢在中国北方土壤环境中的腐蚀行为 [J]. 电镀与涂饰, 2021, 40: 1646
|
16 |
Li H L, Wan H X, Du C W. Corrosion behavior of galvanized steel in typical soil environments [J]. Corros. Prot., 2018, 39: 387
|
|
李海玲, 万红霞, 杜翠薇. 镀锌钢在多种典型土壤环境中的腐蚀行为 [J]. 腐蚀与防护, 2018, 39: 387
|
17 |
Hamlaoui Y, Tifouti L, Pedraza F. Corrosion behaviour of molybdate-phosphate-silicate coatings on galvanized steel [J]. Corros. Sci., 2009, 51: 2455
doi: 10.1016/j.corsci.2009.06.037
|
18 |
Zhai S X, Yang X Y, Yang J L, et al. Corrosion properties of quenching-partitioning-tempering steel in simulated seawater [J]. J. Chin. Soc. Corros. Prot., 2020, 40: 398
|
|
翟思昕, 杨幸运, 杨继兰 等. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究 [J]. 中国腐蚀与防护学报, 2020, 40: 398
|
19 |
Wan H X, Song D D, Liu Z Y, et al. Effect of alternating current on corrosion behavior of X80 pipeline steel in near-neutral environment [J]. Acta Metall. Sin., 2017, 53: 575
|
|
万红霞, 宋东东, 刘智勇 等. 交流电对X80钢在近中性环境中腐蚀行为的影响 [J]. 金属学报, 2017, 53: 575
|
20 |
Mokaddem M, Volovitch P, Ogle K. The anodic dissolution of zinc and zinc alloys in alkaline solution. I. Oxide formation on electrogalvanized steel [J]. Electrochim. Acta, 2010, 55: 7867
doi: 10.1016/j.electacta.2010.02.020
|
21 |
Yan C Q, Liu Y L, Zhang J, et al. Synergistic effect of glycine and BTA on step height reduction efficiency after copper CMP in weakly alkaline slurry [J]. ECS J. Solid State Sci. Technol., 2017, 6: P1
doi: 10.1149/2.0291612jss
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|