水蒸气对Ni-20Cr合金及其溅射微晶涂层1000℃氧化行为的影响

中国腐蚀与防护学报

2001, Vol. 21

Issue (2): 95-100

研究报告

本期目录 | 过刊浏览

水蒸气对Ni-20Cr合金及其溅射微晶涂层1000℃氧化行为的影响

耿树江;王福会

中科院金属所;金属腐蚀与防护国家重点实验室

EFFECT OF WATER VAPOR ON HIGH-TEMPERATURE OXIDATION BEHAVIOR OF Ni-20Cr ALLOY AND ITS SPUTTEREDMICROCRYSTALLINE COATING AT 1000℃

;

中科院金属所;金属腐蚀与防护国家重点实验室

全文: PDF(213 KB)

摘要: 研究了Ni-20Cr合金及其溅射微晶涂层在1000℃下H2O/ O 2中的氧化行为.结果表明:该合金在水蒸气中的氧化增重随着水蒸气的增加而减小,而且水蒸气的含量影响氧化膜的组成.对于溅射微晶涂层,水蒸气的含量只影响氧化增重.通过金相、X射线衍射、SEM(带有EDX)观察分析了氧化产物．提出了水蒸气的作用机制.

关键词 ：水蒸气, Ni-20Cr合金, 溅射微晶涂层, 氧化行为

Abstract：The oxidation behavior of Ni-20Cr alloy and its spu ttered microcrystalline coating have been studied in the presence of water vapor at 1000℃.The results indicate that the higher the water vapor content,the le ss the mass gain of the alloy.The composition of scale depends on the content o f water vapor.However,the water vapor content has only effect on the mass gain of the microcrystalline coating.The oxide scales were examined and analyzed by optical microscope(OM),X-ray diffraction(XRD) and scanning electron microscope (SEM) with EDX.The mechanism of the effect of water vapor on the alloy and its sputtered microcrystalline coatings was proposed.

Key words： water vapor Ni-20Cr alloy sputtered microcrystalline c oating oxidation mechanism

收稿日期: 2000-05-20

ZTFLH:

TG172.8

通讯作者: 耿树江

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	耿树江
	王福会
44.8K

引用本文:

耿树江; 王福会 . 水蒸气对Ni-20Cr合金及其溅射微晶涂层1000℃氧化行为的影响[J]. 中国腐蚀与防护学报, 2001, 21(2): 95-100 .
. EFFECT OF WATER VAPOR ON HIGH-TEMPERATURE OXIDATION BEHAVIOR OF Ni-20Cr ALLOY AND ITS SPUTTEREDMICROCRYSTALLINE COATING AT 1000℃. J Chin Soc Corr Pro, 2001, 21(2): 95-100 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2001/V21/I2/95

[1]WoodGC ,HodgkiessT .Characteristicscalesonpurenickel -chromiumalloysat 80 0°～ 12 0 0℃ [J].J .Electrochem .Soc .,196 6 ,113:319
[2 ]DouglassDL .TheOxidationmechanismofdiluteNi-Cralloys[J].CorrosionSci.,196 8,8:6 6 5
[3]ChattopadhyayB ,WoodGC .Thetransientoxidationofalloys[J].Oxid .Met .,1970 ,2 :373
[4 ]StoottFH ,WoodGC ,StringerJ.Theinfluenceofalloyingelementsonthedevelopmentandmaintenanceofprotectivescales[J].Oxid .Met.,1995 ,44 :113
[5 ]BennetMJ ,BellamyBA ,KnightCF ,etal.Improvementbyceriumandyttriumionimplantationoftheoxidationbehaviorofa 2 0Cr- 2 5Niniobium -stabilizedstainlesssteelinCO2 [J].Mater.Sci.Eng .,1985 ,6 9:35 9
[6 ]GigginsCS ,PettitFS .Theeffectofalloygrain -sizeandsurfacedeformationontheselectiveoxidationofchromiuminNi-Cralloysattemperaturesof 90 0℃and 110 0℃ [J].Trans.Metall.Soc .AIME ,196 9,2 45 :2 5 0 9
[7]WoodGC ,WrightIG ,HodgkiessT ,WhittleDP .AcomparisonoftheoxidationofFe-Cr,Ni-CrandCo -Cralloysinoxy genandwatervapor[J].Werkst.Korrs.,1970 ,2 1:90 0
[8]FryburgGC ,MillerRA ,KohlFJ ,StearnsCA .VolatileproductsinthecorrosionofCr,Mo ,TiandfoursuperalloysexposedtoO2 containingH2 OandgaseousNaCl[J].J .Electrochem .Soc .,1977,12 4:1738
[9]StringerJ,WrightIG .Thehigh -temperatureoxidationofcobalt- 2 1wt.%chromium - 3vol.%Y2 O3 alloys[J].Oxid .Met.,1972 ,5 :5 9
[10 ]GigginsCS ,PettitFS .OxidationofNi-Cralloysbetween 80 0℃and 12 0 0℃ [J].Trans .TMS -AIME ,196 9,2 45 :2 495
[11]AtkinsonA ,TaylorRI.Transportinnon -stoichiometriccompounds[M ].SimkovichStubicanVS ,eds.NewYork :Plenum ,1985 ,2 85
[12 ]BennettMJ ,MoonDP .inTheRoleofActiveElementsintheOxidationBehaviorofHighTemperatureMetalsandalloys[M ].LangE ,ed .London :Elsevier ,111
[13]WangF .High -temperaturemicrocrystallinecoatings[D].PhDdissertation ,InstituteofCorrosionandProtectionofMetals,ChineseAcademyofSciences,1992

[1]	王成; 江峰; 王福会 . 有机硅涂层对304不锈钢在400℃盐和水蒸气综合作用下的防护作用[J]. 中国腐蚀与防护学报, 2005, 25(3): 149-151 .
[2]	耿树江; 朱圣龙; 王福会 . 纯Ni在600℃～700℃固态NaCl和水蒸气综合作用下的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(5): 262-265 .
[3]	李辛庚; 何家文 . 喷丸处理提高TP304H耐热钢锅炉管抗水蒸气氧化性能应用效果的观察[J]. 中国腐蚀与防护学报, 2003, 23(3): 171-174 .
[4]	李铁藩 . 金属晶界在高温氧化中的作用[J]. 中国腐蚀与防护学报, 2002, 22(3): 180-183 .
[5]	于京升; 周春根; 徐惠彬; 宫声凯 . 水蒸气对NiCrAlY涂层抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2002, 22(2): 88-91 .
[6]	李辛庚; 王学刚; 何家文 . 喷丸与电泳沉积稀土薄膜复合处理提高T91钢抗水蒸气氧化性能的研究[J]. 中国腐蚀与防护学报, 2002, 22(2): 101-104 .
[7]	李瑛; Y.BABA; T.SEKIGUCHI . 304不锈钢氧离子溅射的同步辐射光电子能谱原位研究Ⅰ.钢中金属元素的氧化行为[J]. 中国腐蚀与防护学报, 2000, 20(6): 321-330 .
[8]	舒勇华; 王福会; 吴维tao . NaCl盐膜和水蒸气对纯Cr腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2000, 20(2): 88-96 .
[9]	沈嘉年;王戈. Ni-20Cr合金的高温氯化[J]. 中国腐蚀与防护学报, 1995, 15(3): 189-195.

Viewed

Full text

Abstract

Cited

Shared

Discussed