几种含铌镍基合金的热腐蚀研究

左禹;朱日彰;郭曼玖

北京钢铁学院;北京钢铁学院;冶金部钢铁研究总院

HOT CORROSION BEHAVIOR OF SOME Ni-BASE ALLOYS CONTAINING Nb

Zuo Yu Zhu Rizhang (Beijing University of Irom and Steel Technology) Guo Manjiou (Central Iron and Steel Research Institute)

全文: PDF(2551 KB)

摘要: 用硫酸钠沉积法研究了四种镍基合金-Ni-16Cr,Ni-16Cr-2Nb,IN738和537合金-在900～1000℃之间的热腐蚀行为。用热天平测量了热腐蚀动力学曲线,用金相、SEM、电子探针、X 射线衍射和~(3δ)S 示踪法观察和分析了腐蚀产物。研究发现,Ni-16Cr-2Nb 合金中的铌富集在表面氧化膜内,形成 NaNbO_3而降低熔盐中的 O~(2-)浓度,抑制 Cr_2O_3膜与熔盐的反应;但在复杂成份的合金中。铌的上述作用可能促进氧化膜的酸性熔融。鈪同时能促进硫在 Ni-16Cr-2Nb 变形合金晶界上的连续分布,加速内硫化过程。

Abstract：The hot corrosion behavior of four Ni-based alloys—Ni-16Cr,Ni-16Cr-2Nb, IN738 and 537—between 900～1000℃ were studied by the use of Na_2SO_4 deposit. The kinetics curves of hot corrosion were obtained by using a thermobalance. Corrosion products were examined with metallography,SEM,electronic microprobe,X-rays diffraction and ~(36)S tracer.It was found that Nb was enriched in surface oxide scale of Ni-16Cr-2Nb.Nb could decrease the O~(2-) ion activity of Na_2SO_4,melts by the formation of NaNbO_3,and then reaction between Cr_2O_3 scale and the melts was retarded.For multi-component alloys like IN738 and 537,Nb might promote acidic fluxing of the oxide scale.Nb also promoted continuous segregation of sulfur at grain boundaries of Ni-16Cr- 2Nb alloy and speed up the process of internal sulfidation.

收稿日期: 1985-04-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	左禹
	朱日彰
	郭曼玖
44.8K

引用本文:

左禹;朱日彰;郭曼玖. 几种含铌镍基合金的热腐蚀研究[J]. 中国腐蚀与防护学报, 1985, 5(2): 110-116.
. HOT CORROSION BEHAVIOR OF SOME Ni-BASE ALLOYS CONTAINING Nb. J Chin Soc Corr Pro, 1985, 5(2): 110-116.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1985/V5/I2/110

[1] Johnson,D.M.;Whittle,D.P.;Stringer,J.,Corro.Sci.,15,721(1975)
[2] JOhnson,D.M.;et al,Oxid.Met.,12,273(1978)
[3] 张匀;赵洪恩;郭延芬;刘嘉乐,中国腐蚀与防护学报,3(1) ,46(1983)
[4] 郭曼玖;左禹;朱日彰,理化检验,物理分册,即将发表。
[5] Erds,E;Denzler,E,Behavior of High Temperature Alloys in Aggressive Environments,[Proc.Conf],Petten,The Netherlands,Oct.1979,455(1980)
[6] Seybolt.A;U.,Na_2SO_4-Superalloy Corrosion Mechanism Studies,General Electric Technical Information Series,70-C-189(June 1970)
[7] Goebel,J.A.;Pettit,F.S.,Met.Trans.,4,261(1973)
[8] Pettit,F.S.,Hot Corrosion Degradation of Metals and Alloys-a United Theory,AD-AO72645(June 1979)
[9] Goebel,J.A.;Pettit,F.S.,Met.Trans.,1,1943(1970)
[10] Rapp,R.A.;Goto,K.S.,Proc.“Second Intern.Symposium on Molten Salts”,J.Braunstein ed.,The Electrochem.Soc.,(1979)
[11] Samsonov,G.V.,The Oxide Hand book,Second Edition,IFI/Plenum Data Company,New York,(1982)
[12] Fryburg,G.C.;et al,J.Electrochem.Soc.,124,1147(1977)
[13] Shatynski,S.R.,Oxid.Met.,11,307(1977)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed