中国腐蚀与防护学报  1985, Vol. 5 Issue (2): 79-91    
  研究报告 本期目录 | 过刊浏览 |
Fe-Cr-Mo系铁素体不锈钢在氯化物介质中的实验电位-pH图研究
杨武;华惠中
上海材料研究所;上海材料研究所
AN INVESTIGATION OF THE EXPERIMENTAL POTENTIAL-pH DIAGRAMS FOR Fe-Cr-Mo FERRITIC STAINLESS STEELS IN CHLORIDE MEDIA
Fang Wu Hua Huizhong (Shanghai Research Institute of Materials)
全文: PDF(972 KB)  
摘要: 通过测定合金在含 1N Cl~-的不同 pH 值的水溶液中的阳极极化曲线,绘制了三个系列的12种铁素体不锈钢(17Cr-xMo,25Cr-xMo,30Cr-xMo,其中 x=0、2、4、6)的实验电位-pH 图。合金中的 Cr 含量对点蚀起始过程影响极为显著;Mo 含量对点蚀击穿电位的影响则与合金中 Cr 含量有密切关系。添加少量的 Mo 可使低电位、低 pH 值条件下的活化腐蚀区大大缩小,因而对局部腐蚀的发展过程起重要的阻滞作用;Cr 也有类似的影响,但远不及 Mo 的影响那么明显和意义重大。适量的 Cr 和 Mo 的综合作用可使合金具有抵抗局部腐蚀发生及发展的优良性能。
Abstract:The experimental potential-pH diagrams for three groups of ferritic stainless steels(17Cr-xMo,25Cr-xMo and 30Cr-xMo,where x=0,2,4,6)in 1N C1~- solutions at 25℃ have been established through measuring the anodic polarization curves of these alloys in solutions with various pH values.The chromium contents in the alloys show significant effect on the initiation of pitting,while the effect of molybdenum contents on pitting breakdown potentials strongly depends on the chromium levels in the alloys.Small additions of molybdenum to Fe-Cr alloys result in remarkable shrinkage of the active corrosion region at lower pH and lower potentials,and thus exert significant inhibition effect on the propagation of localized comosion.Chromium also shows some influence on this active region,but this effect is much less signifi- cant than that of molybdenum.The synergic role of chromium and molybdenum at proper levels would be beneficial for the super-performance alloys to effect- ively resist the initiation and propagation of localized corrosion.
收稿日期: 1985-04-25     

引用本文:

杨武;华惠中. Fe-Cr-Mo系铁素体不锈钢在氯化物介质中的实验电位-pH图研究[J]. 中国腐蚀与防护学报, 1985, 5(2): 79-91.
. AN INVESTIGATION OF THE EXPERIMENTAL POTENTIAL-pH DIAGRAMS FOR Fe-Cr-Mo FERRITIC STAINLESS STEELS IN CHLORIDE MEDIA. J Chin Soc Corr Pro, 1985, 5(2): 79-91.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y1985/V5/I2/79

[1] Pourbaix,M.Atlas of Electrochemical Equilibria in Aqueous Solutions,Pergamon Press,(1966)
[2] Pourbaix,M.,Lectures on Electrochemical Corrosion,Plenum Press,(1973)
[3] Pourbaix,M.,Localized Corrosion,Ed.,Staehle R.W.,et al,NACE-3,12(1974)
[4] Pourbaix,M.,J.Electrochem.Soc.,123(2) ,25c(1976)
[5] 杨武,机械工程材料,7(1) ,14(1983)
[6] Verink,Jr.E.D.;Pourbaix,M.Corrosion,27(12) ,495(1971)
[7] Verink,Jr.E.D.,Electrochemical Techniques for Corrosion,Ed.Baboian,R.,NACE,43(1977)
[8] Verink,Jr.E.D.,Corrosion,38(6) ,336(1982)
[9] Verink Jr.E.D.;Lee,T.S.;Cusumana,R.L.,Corrosion,28(9) ,348(1972)
[10] Heidersbach,Jr.R.H;Verink,Jr.E.D.,Corrosion,28(11) ,397(1972)
[11] Laliberte,L.H.;Mueller,W.A,,Ref.[7] ,11(1977)
[12] Mor,E.D.;Scotto,V.;Mollica A.Werkstoffe und Korrosion,31(4) ,281(1980)
[13] 下平三郎.日本金属学会会报,16(2) ,89;16(3) ,157(1977)
[14] Steigerwald.R.F.;Bond,A.P.;Dundas,H.J.;Lizlovs,E.A.,Corrosion,33(8) ,279(1977)
[15] Lizlovs,E.A.;Bond,A.P.,J.Electorchem.Soc.,116(5) ,574(1969)
[16] Lizlovs,E.A.;Bond,A.P.,J.Electorchem.Soc.,118(1) ,22(1971)
[17] Bond,A.P.,J.Electrochem.Soc.,120(5) ,603(1973)
[18] Lizlovs,E.A.;Bond,A.P.,J.Electrochem.Soc.,122(6) ,719(1975)
[19] Galvek,J.R.;Lumsden,J.B.;Staehle,R.W.,J,Electrochem.Soc.,125(8) ,1204(1978)
[20] Weast,R.C.,Ed.,CRC Handbook of Chemistry and Physics,CRC Press.Inc.D-133(1977)
[21] Yang,W.(杨武);Pourbaix,A.,(a)Rapports Techniques CEBELCOR,141,RT262(1981) [b]中国腐蚀与防护学报,3(1) ,22(1983)
[21] (a)Yang,W.(杨武);Ni,R.C.(倪瑞澄);Hua,H.Z.(华惠中);Pourbaix,A.,Corrosion Sci.,24(8) ,691(1984)
[22] Kolotyrkin,J.M.,Corrosion.19(8) ,261t(1963)
[23] Steigerwald,R.F.,Corrosion,22(4) ,107(1966)
[24] 安保秀雄,野口栄,林巨幸,金属材料,13(11) ,74(1973)
[25]#12
[26] Szklarska-Smialowska,Z.,The Proceedings of the 7th ICMC.,14(1978)
No related articles found!