硅的添加量对铝锌合金热镀层的组织及耐蚀性的影响

孟荣祥;杨熙珍

山东工业大学;山东工业大学

MICROSTRUCTURE OF THE 55％ Al-Zn ALLOY COATING ADN INFLUENCE OF SILICON CONTENT ON ITS CORROSION BEHAVIOUR

Meng Rongxiang and Yang Xizhen(Shandong Engineering Institute)

全文: PDF(2254 KB)

摘要: 作者研究了硅的添加量对55％Al-Zn-1.6％Si合金热镀层组织形貌及耐蚀性的影响。结果证明,少量的硅(1～2％之间)对合金组织及耐蚀性基本上无影响;而过量的硅(>2％)将以硅化物或单体硅的形式在枝晶间富锌伪共晶相中析出,从而加大镀层合金表面的电化学不均匀性,降低其耐蚀性。应用计算机解析计算了由多相组成的电极上的腐蚀电流,并结合应用模拟相方法定量描述了此合金镀层的耐蚀性随硅含量的变化关系。

Abstract：The influence of additive amount of Si on the microstructure and corrosion behaviour of 55％ Al-Zn-1.6％Si alloy hot-dip coating has been investigated. It is shown that small amount of si (1～20％) had little influence on the microstructure and corrosion resistance while amount of Si>2％ would show up free crystals of Si or silicon compounds condensed together with the interdendritic quasi-eutectic Zn-rich phase thereby increasing the electrochemical heterogeneity of the coating and decreasing its corrosion resistance.The corrosion current density of each phase on the multiphase electrode has been calculated by computerizing technique, combined with the simulating phase method. The relation between the corrosion rate of the coating and the additive amount of Si has been founded quantitatively.

收稿日期: 1986-04-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	孟荣祥
	杨熙珍
44.8K

引用本文:

孟荣祥;杨熙珍. 硅的添加量对铝锌合金热镀层的组织及耐蚀性的影响[J]. 中国腐蚀与防护学报, 1986, 6(2): 91-102.
. MICROSTRUCTURE OF THE 55％ Al-Zn ALLOY COATING ADN INFLUENCE OF SILICON CONTENT ON ITS CORROSION BEHAVIOUR. J Chin Soc Corr Pro, 1986, 6(2): 91-102.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1986/V6/I2/91

[1] Zoccola, J.C., et al., ASTM STP 646, S.K., Coburn, Ed, 165～184(1978)
[2] Townsend, H.E., et al., Mater. Perf., 18 (10) , 13～20(1979)
[3] Townsend, H.E., et al., Mater. Perf., 2281 (1) , 54(1983)
[4] Beickwede, D.J., Intern.Conf on Production and Use Coil-Coated, Birming-ham, 30, Sept., (1930)
[5] US Pat. 3, 343, 930; 3, 393, 089
[6] Sivan, V., et al., Metal Finishing, 9, 48～51(1978)
[7] 孟荣祥,硅在55％Al-Zn合金热镀层形成过程中的作用,山东工业大学学位论文,(1985)
[8] 山东工业大学金属腐蚀与防护研究室,热镀Al-Zn合金科研报告,(1984)
[9] Agarwal, S.B., et al., Mater.Perf., 22(10) , 19～23(1983)
[10] 杜爱玲;杨熙珍,中国腐蚀与防护学报,6(2) ,81(1986)
[11] Murray, J.L., Bulletin of Alloy Diagrams, 4(1) , 55～73(1983)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed