GH33合金在700℃SO_2/空气环境中受载时的热腐蚀

胡赓祥;周浪;张源虎

上海交通大学;上海交通大学;上海交通大学

HOT CORROSION OF A Ni-BASE SUPERALLOY IN SO~2/AIR ENVIRONMENT UNDER APPLIED LOAD

Hu Gengxiang Zhou Lang Zhang Yuanhu(Shanghai Jiao Tong University)

全文: PDF(1994 KB)

摘要: <正> 高温合金在含硫-氧环境中的行为已开始引起重视。已有的工作表明,单一地研究合金的高温腐蚀不能充分反映合金在使用条件下的行为和破坏倾向,必需了解在高温腐蚀环境和应力复合作用下的特性,才能为使用合金和研制新合金提供可靠的依据。本工作应用自制的可控制环境气氛的高温持久试验装置,以含SO_2的气氛为环境介质,研究了GH33合金在含硫氧化环境和外加应力的复合作用下产生的热腐蚀现象,并对其有关机理作了分析探讨。

Abstract：Hot corrosion of GH33 Ni-base superalloy was investigated by conducting creep tests in an environmental chamber circulated with SO_2-air mixed gas. Analyses were carried out on the outer surfaces, longitudinal sections and fracture surfaces of the tested specimens, including specimens tested to rupture or interrupted at various extents of creep strain. The results were compared with those tested in air.It was found that both in air and in SO_2/air environment a Cr-riched oxide scale was formed initially, which protected the grain boundaries and matrix from being attacked by SO_2. Therefore, as long as the protective scale was not ruptured by the creep deformation, SO_2/air and air played the same role in corrosion, i. e. oxidation is the principal process. But after the deformation increased to a certain extent, intergranular cracks initiated on the specimen surface and sulfur attack occurred. Molten Ni-Ni_3S_2 eutectics formed at grain boundaries which led to catastrophic corrosion and premature failure of the specimen.The mechanism of such corrosion process is discussed. It is suggested that the interaction of hot corrosion and creep of superalloy greatly accelerated the failure process and attention should be paid to this problem during engineering design or material application.

收稿日期: 1987-02-25

基金资助:中国科学院科学基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	胡赓祥
	周浪
	张源虎
44.8K

引用本文:

胡赓祥;周浪;张源虎. GH33合金在700℃SO_2/空气环境中受载时的热腐蚀[J]. 中国腐蚀与防护学报, 1987, 7(1): 67-72.
. HOT CORROSION OF A Ni-BASE SUPERALLOY IN SO~2/AIR ENVIRONMENT UNDER APPLIED LOAD. J Chin Soc Corr Pro, 1987, 7(1): 67-72.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1987/V7/I1/67

[1] Hocking, M. G.: Vasantasree, V., Corrosion Science.,16, 279 (1976)
[2] Sidky, P. S.; Hocking, M. G., Behaviour of High Temperature Alloys in Agressive Enviroments., 497 (1979)
[3] Chang, D. R.; Nemoto, R.: Wagner, Jr. J. B.. Met. Trans. A 7A, 803(1976)
[4] Worrell, L.: Rao. B. K., High Temperature Corrosicn 297(1983)
[5] Hancock. P., International Congress on Metallic Corrosicn 193 (1962)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed