钢在中性水溶液中腐蚀疲劳的研究

李明奇;冯博学;魏振伟

兰州大学物理系;兰州大学物理系;兰州大学物理系

THE CORROSON FATIGUE OF STEELS IN NEUTRAL AQUEOUS SOLUTION

Li Mingqi Feng Boxue and Wei Zhenwei (Dept. of Physics; University of Lanzhou)

全文: PDF(1316 KB)

摘要: 本文对16Mn、08PVXt、440C和4340钢在蒸馏水和3.5％NaCl水溶液中的疲劳裂纹扩展速率(FCGR)进行了实验研究,并与一些钢在同类介质中的腐蚀疲劳(CF)实验结果进行了对比。结果表明:一般钢在前种介质中的疲劳寿命(FL)较后者长;08PVXt、440C及4340钢在蒸馏水中的FCGR较NaCl水溶液中高。而16Mn钢则有相反的结果。作者认为,这种情况是由于Cl~-在裂纹萌生和宏观裂纹扩展过程中起的不同作用所致。

Abstract：The fatigue crack growth rate (FCGR) of 08PVXt, 16Mn, 440C and 4340 steels in distilled water anb NaClaqueous solution has been investigated, and the experimental results have been compared with those of corrosion fatigue in the literature. The fatigue life (FL) of of ordinary steels in distilled water is higher then that in NaCl aqueous solution. The FCGR of 08PVXt, 440C and 4340 steels in distilled water is higher than those in NaCl aqueous solution. However, contrary result is observed for the 16Mn steel. The authors are inclined to think that the function of the Cl~- is different in the crack initiation and in the macroscopic crack propagation.

收稿日期: 1987-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李明奇
	冯博学
	魏振伟
44.8K

引用本文:

李明奇;冯博学;魏振伟. 钢在中性水溶液中腐蚀疲劳的研究[J]. 中国腐蚀与防护学报, 1987, 7(4): 257-264.
. THE CORROSON FATIGUE OF STEELS IN NEUTRAL AQUEOUS SOLUTION. J Chin Soc Corr Pro, 1987, 7(4): 257-264.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1987/V7/I4/257

[1] 李明奇,石玥,童志深;中国腐蚀与防护学报;4(1) ,61(1984)
[2] 童志深,候耀永,李明奇,蒋生蕊;金属学报;18(5) ,618(1982)
[3] Tong zhishen, Li Mingqi, Feng Boxue, Shi Yue; Corrosicn 41(3) 121 (1985)
[4] Endo, K; Miyas, Y, Monatsh, 13, 56(1932)
[5] 李春林等;中国金属学会第二次全国疲劳学术会议,重庆,(1984． 11)
[6] 上海钢铁研究所主编;国外海洋用金属材料(腐蚀机理和实验方办);P.10～41(1975)
[7] 徐坚等;腐蚀金属学及耐蚀金属材料 P.70,(1975)
[8] 褚武扬;《断裂力学基础》,科学出版社(1979)
[9] 李明奇,冯博学,童志深;兰州大学 21986)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed