氢对304不锈钢阳极行为的影响

乔利杰;褚武扬;肖纪美;黄华

北京钢铁学院;北京钢铁学院;北京钢铁学院;北京钢铁学院

EFFECT OF HYDROGEN ON ANODIC BEHAVIOR OF 304 STAINLESS STEEL

Qiao Lijie Chu Wuyang Xiao Chimei Huang Hua (Beijino Univ. of Iron and Steel Tech.)

全文: PDF(366 KB)

摘要: <正> 虽然奥氏体不锈钢在42％MgCl_2沸腾溶液中的应力腐蚀并不是由氢致开裂引起的,但在应力腐蚀过程中生成的氢可以进入试样并可在裂纹前沿富集。为澄清进入试样的氢是否对阳极溶解过程产生促进作用,曾有人用失重法、晶间腐蚀和极化曲线变化等研究氢对阳极行为的影响,并得出氢促进阳极溶解的结论。应当指出,充氢试样的阳极电流包括了氢的氧化电流,因此充氢后阳极电流的增大并不证明氢促进了阳极溶解过程。虽然失重法能反映氢的促进作用,但只适用于腐蚀较为严重的情况。

Abstract：Effect of hydrogen on anodic dissolution and passivation of 304 stainless steel has been studied in 1N H_2SO_4+0.1N HCl solution at controlled potentials. Ion concentrations of Fe, Cr and Ni dissolved in the solution are determined using plasma emission spectroscopy. Thus, the amount of net corrosion of the steel containing hydrogen is obtained. The results show that hydrogen promotes strongly anodic dissolution of 304 stainless steel in the transpassive potential region, (E=1.0V, SCE). The rate of dissolution increases with hydrogen content. The ion concentrations of Fe, Cr and Ni in fhe solution under different charging time are analyzed. The ion ratio of Fe, Cr and Ni is about 78:16:6 for uncharged specimen, while it is the same as that of the chemical composition of the steel for hydrogen charged specimen, i.e., Fe:Cr:Ni=72:19:9. This result reveals that hydrogen decreases the stability of passive film. In the passive potential region(E=0.5V), however, hydrogen has little effect on the anodic behavior. The ion ratio is 82:11:7 for both hydrogen charged and uncharged specimens. The amount of net corrosion of the specimens with hydrogen is about equal to that of the specimen without hydrogen.

收稿日期: 1988-04-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	乔利杰
	褚武扬
	肖纪美
	黄华
44.8K

引用本文:

乔利杰;褚武扬;肖纪美;黄华. 氢对304不锈钢阳极行为的影响[J]. 中国腐蚀与防护学报, 1988, 8(2): 148-152.
. EFFECT OF HYDROGEN ON ANODIC BEHAVIOR OF 304 STAINLESS STEEL. J Chin Soc Corr Pro, 1988, 8(2): 148-152.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1988/V8/I2/148

[1] 姚京;褚武扬;肖纪美,金属学报,19,445(1983)
[2] 褚武扬;王核力;马若涛;肖纪美,金属学报,21(1) ,A86(1985)
[3] 乔利杰;褚武扬;肖纪美,金属学报,23(3) ,A228(1987)
[4] 乔利杰;褚武扬;肖纪美,北京钢铁学院学报,(2) ,113(1986)
[5] 乔利杰;褚武扬;肖纪美,中国腐蚀与防护学报,6(4) ,273(1986)
[6] Lijie,Q.(乔利杰),Wuyang,C.(褚武扬);Chimei,X.(肖纪美),Scripta metall,5,(1988)
[7] 赵克清;肖纪美;胡茂圃,中国腐蚀与防护学报,4(3) ,179(1984)
[8] Hasegawa, M.; Osawa, M., Corrosion, 36(2) . 67(1980)
[9] Hasegawa, M.; Osawa, M., Corrosion, 39(4) , 115(1983)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed