预温变形对2O91　Al-Li-Cu-Mg-Zr合金应力腐蚀敏感性的影响

李仁顺;王佐义

哈尔滨工业大学

THE EFFECT OF WARM-ROLLING POOR TO AGING ON STRESS CORROSION CRACKING SUSCEPTIBILITY OF ALUMINIUM ALLOY 2O91

Li Renshun; Wang Zuoyi(Harbin Institute of Technology)

全文: PDF(1962 KB)

摘要: 用慢应变速率拉伸试验和三点弯曲恒应变试验研究不同温度下预轧制变形对２０９１合金应力腐蚀敏感性的影响．透射电镜显微组织分析表明，温轧预变形处理可减少晶界上Ｔ２相的数量，增加晶内沉淀相（σ＇和Ｓ＇相）的体积分数，使合金对应力腐蚀的抗力得到明显提高．经１８０℃温轧预变形处理的合金具有最低的应力腐蚀敏感性．

关键词 ：２０９１Ａｌ－Ｌｉ－Ｃｕ－Ｍｇ－Ｚｒ合金, 温轧预变形, 应力腐蚀敏感性

Abstract：The influence of warm-rolling at different temperatures prior to aging on the stress corrosion cracking sareptibility of Al-Li-Cu-Mg-Zr alloy 2091 has been studied by slow strain rate tests and constant strain tests with threepoiot loading samples. The examination of microstructure of the alloy by TEM shows that warm-rolling prior tO aging reduces the amount of T2 precipitates and enhances the volume of δ' and S' phare within grains. As a result, the SCC resistance of the alloy is sipecatly improved. The alloy rorolled at 180℃ prior to aging possesses the lowest SCC susceptibility.

Key words： Al-Li-Cu-Mg-Zr alloy 2091 Warm-rolling SCC susceptibility

收稿日期: 1995-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李仁顺
	王佐义
44.8K

引用本文:

李仁顺;王佐义. 预温变形对2O91　Al-Li-Cu-Mg-Zr合金应力腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 1995, 15(1): 15-20.
. THE EFFECT OF WARM-ROLLING POOR TO AGING ON STRESS CORROSION CRACKING SUSCEPTIBILITY OF ALUMINIUM ALLOY 2O91. J Chin Soc Corr Pro, 1995, 15(1): 15-20.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1995/V15/I1/15

1WeissI,JonasJJ．Metall,Thans,1979,10A:8312AudierM,GuyotP．ActaMetall．;1988,36(5):13213陈想平．哈尔滨工业大学硕士学位论文(1991)4PatonNE,SommerAWThirdInt．Conf．StrengthofMetalsandAlloys．1973．3:1015NessEActaMetall,1971,20:499

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed