BTA和PTD对铜的缓蚀作用的光电响应研究

汪知恩;周国定;徐群杰

上海电力学院电化学研究室;上海200090;上海电力学院电化学研究室;上海200090;华东理工大学精细化工系;上海200237

A STUDY OF PHOTORESPONSE FOR COPPER CORROSION INHIBITION BY BTA AND PTD

WANG Zhi-en ZHOU Guo-ding XU Qun-jie (Electrochemical Research Group; Shanghai Institute of Electric Power; Shanghai 200090)

全文: PDF(404 KB)

摘要: 用光电化学方法研究了铜电极在含缓蚀剂BTA和PTD的硼砂和硼砂-硼酸缓冲溶液中的光电化学行为,研究了不同浓度缓蚀剂对铜电极表面Cu_2O完全还原为Cu的电位φ_v的影响。试验结果表明φ_v表征了缓蚀剂所形成的膜与Cu_2O层之间的结合力,缓蚀作用越强则φ_v越负。

关键词 ：钢电极, 缓蚀作用, 光电响应, BTA, PTD

Abstract：The inhibition behaviour of BTA and PTD in borax solution for copper was studied by using pho-toelectrochemical technique. The potential φv, at which Cu2O on the electrode was completely reduced to Cu, was applied to characterize the interaction of Cu2O layer with the film, for example, Cu(I) BTA, formed from inhibitor on the Cu electrode. The more negative the φv, the more efficient the inhibitor. BTA might function as stabilizing Cu2O film on the surface. The corrosion resistance of copper was dependent on the Cu2O film. The inhibitive action of both BTA and PTD on Cu electrode was compared by photoelectrochemical method. The results were in agreement with those of ac impedance measurements.

Key words： Copper electrode Inhibition Photoresponse BTA PTD

收稿日期: 1998-02-25

基金资助:国家自然科学基金资助项目;上海市高校青年科学基金项目

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	汪知恩
	周国定
	徐群杰
44.8K

引用本文:

汪知恩;周国定;徐群杰. BTA和PTD对铜的缓蚀作用的光电响应研究[J]. 中国腐蚀与防护学报, 1998, 18(1): 57-61.
. A STUDY OF PHOTORESPONSE FOR COPPER CORROSION INHIBITION BY BTA AND PTD. J Chin Soc Corr Pro, 1998, 18(1): 57-61.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1998/V18/I1/57

1 Wilhelm S M, Tanizawa Y, Liu Chang-Yi, Hackerman N. Corros. Sci., 1982, 22:791
2 Modestov A D, Zhou Guo-Ding, Ge H H, Loo B H. J. Electroanal. Chem., 1995, 308:63
3 周国定,Modestov A D, 潘传智,杨迈之,蔡生民.物理化学学报,1995, 11:51
4 Liu X Y, Zhou Guo-Ding, Yang M Z, Cai S M, Loo B H. J. Electroanal. Chem., 1993, 361:265
5 Modestov A D, Zhou Guo-Ding, Wu Y P, Notoya T, Schweinsherg D P. Corros. Sci., 1994, 36:1931
6 邵华,周国定,杨迈之,蔡生民.化学学报,1996,54:325
7 高永丰,邵华,徐群杰,吴一平,周国定.材料保护,1995, 28:9
8 Notoya T, Poling G W. Corrosion, 1976, 32:216
9 Chadwick D, Hashemi T. Corros. Sci., 1978, 18:39
10 Fox P G, Lewis G, Boden P J. Corros. Sci., 1979, 19:457
11 Tromans D, Sun Ru-hong. J. Electrochem. Soc., 1991, 138:3235
12 El-taib Heakal F, Haruyama S, Corros. Sci., 1980, 20:887

[1]	吕祥鸿,张晔,闫亚丽,侯娟,李健,王晨. 两种新型曼尼希碱缓蚀剂的性能及吸附行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[2]	王海媛, 卫英慧, 杜华云, 刘宝胜, 郭春丽, 侯利锋. 绿色缓蚀剂SDDTC对AZ31B镁合金的缓蚀作用及吸附行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 62-67.
[3]	闫涛,宋振纶,杨丽景,肖涛,侯利锋. 新喀里多尼亚弧菌对Cu在人工海水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(2): 157-164.
[4]	张大全,谢彬,李瑾,何先明,高立新. 谷氨酸自组装膜对铜的缓蚀机理研究[J]. 中国腐蚀与防护学报, 2011, 31(1): 56-61.
[5]	李瑛 . AZ91D 镁合金手汗腐蚀机理研究 Ⅱ手汗模拟液中尿素对AZ91D腐蚀的缓蚀机制研究[J]. 中国腐蚀与防护学报, 2004, 24(6): 334-338 .
[6]	张大全; 高立新; 汪知恩 . NaCl溶液中烷基咪唑对铜的缓蚀作用研究[J]. 中国腐蚀与防护学报, 2002, 22(4): 237-240 .
[7]	徐群杰; 周国定; 陆柱 . 苯并三氮唑及其衍生物在硫酸溶液中对铜的缓蚀作用[J]. 中国腐蚀与防护学报, 2001, 21(3): 172-176 .
[8]	闫丽静; 杨帆; 林海潮 . 长碳链多胺类系列化合物对铁在含H2S的硫酸溶液中的缓蚀作用[J]. 中国腐蚀与防护学报, 2001, 21(1): 19-25 .
[9]	杨文忠; 周本省 . N-磺酸基-氨基二甲叉磷酸缓蚀阻垢剂缓蚀作用的研究[J]. 中国腐蚀与防护学报, 2000, 20(2): 105-110 .
[10]	闫丽静; 林海潮; 吴维tao . 含H2S的硫酸溶液中丙炔醇对铁腐蚀的抑制作用*[J]. 中国腐蚀与防护学报, 1999, 19(4): 221-226 .
[11]	唐子龙; 宋诗哲 . 缓蚀剂哌啶在不锈钢钝化膜表面吸附行为的量子化学从头算研究*[J]. 中国腐蚀与防护学报, 1999, 19(2): 65-71 .
[12]	张大全;俞路;陆柱. 苯并噻唑衍生物的缓蚀作用及PPP量子化学研究[J]. 中国腐蚀与防护学报, 1998, 18(4): 307-310.
[13]	唐子龙. 孔蚀发展过程动力学分析[J]. 中国腐蚀与防护学报, 1998, 18(4): 241-250.
[14]	牟战旗;梁成浩. 不同模拟体液及pH值变化对人体用金属生物材料耐蚀性能的影响[J]. 中国腐蚀与防护学报, 1998, 18(2): 126-130.
[15]	王周成;苏方腾;辜志俊;张瀛洲;周绍民. 离子选择性酚醛涂层对铜在3%NaCl中电化学行为的影响[J]. 中国腐蚀与防护学报, 1997, 17(2): 93-98.

Viewed

Full text

Abstract

Cited

Shared

Discussed