组织配分对双相不锈钢微区极化行为及点蚀抗性的影响 |
汪毅聪, 胡骞, 黄峰, 刘静() |
武汉科技大学 省部共建耐火材料与冶金国家重点实验室 湖北省海洋工程材料及 服役安全工程技术研究中心 武汉 430081 |
|
Effect of Microstructure Partition on Micro-polarization Behavior and Pitting Resistance of Duplex Stainless Steel |
WANG Yicong, HU Qian, HUANG Feng, LIU Jing() |
State Key Laboratory of Refractories and Metallurgy, Hubei Engineering Technology Research Center of Materials and Service Safety, Wuhan University of Science and Technology, Wuhan 430081, China |
引用本文:
汪毅聪, 胡骞, 黄峰, 刘静. 组织配分对双相不锈钢微区极化行为及点蚀抗性的影响[J]. 中国腐蚀与防护学报, 2021, 41(5): 667-672.
Yicong WANG,
Qian HU,
Feng HUANG,
Jing LIU.
Effect of Microstructure Partition on Micro-polarization Behavior and Pitting Resistance of Duplex Stainless Steel. Journal of Chinese Society for Corrosion and protection, 2021, 41(5): 667-672.
链接本文:
https://www.jcscp.org/CN/10.11902/1005.4537.2020.210
或
https://www.jcscp.org/CN/Y2021/V41/I5/667
|
1 |
Feng H, Zhou X Y, Liu H, et al. Development and trend of hyper duplex stainless steels [J]. J. Iron Steel Res., 2015, 27(4): 1
|
1 |
丰涵, 周晓玉, 刘虎等. 特超级双相不锈钢的发展现状及趋势 [J]. 钢铁研究学报, 2015, 27(4): 1
|
2 |
Huang A, Chen J, Song J, et al. Research progress of economic type duplex stainless steel welding [J]. Hot Work. Technol., 2016, 45(5): 7
|
2 |
黄澳, 陈吉, 宋见等. 经济型双相不锈钢焊接的研究进展 [J]. 热加工工艺, 2016, 45(5): 7
|
3 |
Liu Z Y, Li C G, Zhao Y, et al. Control on microstructures and properties of economical duplex stainless steel and its manufacturing technology [J]. Angang Technol., 2016, (2): 1
|
3 |
刘振宇, 李成刚, 赵岩等. 节约型双相不锈钢组织性能控制与制造技术 [J]. 鞍钢技术, 2016, (2): 1
|
4 |
Zhang W Y, Hou S Z. Progress of the application of duplex stainless steel at home and abroad [J]. Mag. Equip. Mach., 2015, (3): 62
|
4 |
张文毓, 侯世忠. 国内外双相不锈钢的应用进展 [J]. 装备机械, 2015, (3): 62
|
5 |
Wang G, Guo Y D, Guo L, et al. Development of duplex stainless steel, characteristics and applications [J]. Sci. Technol. Innovat., 2015, (7): 91
|
5 |
王刚, 郭幼丹, 郭雷等. 双相不锈钢的发展、特点及其应用 [J]. 科技与创新, 2015, (7): 91
|
6 |
Yu H C, Yan Y H, Liu X Y, et al. Analysis on composition, properties and precipitated phases of duplex stainless steel [J]. Spec. Steel, 2019, 40(3): 53
|
6 |
于海成, 严与辉, 刘小杨等. 双相不锈钢成分、性能及析出相分析 [J]. 特殊钢, 2019, 40(3): 53
|
7 |
Otake A, Muto I, Chiba A, et al. Pitting at the δ/γ boundary of type 304 stainless steel in NaCl solution: The role of oxide inclusions and segregation [J]. J. Electrochem. Soc., 2017, 164: C991
|
8 |
Zheng S Q, Li C Y, Qi Y M, et al. Mechanism of (Mg, Al, Ca)-oxide inclusion-induced pitting corrosion in 316L stainless steel exposed to sulphur environments containing chloride ion [J]. Corros. Sci., 2013, 67: 20
|
9 |
Jia D B, Zhong L C, Yu J K, et al. Effects of electropulsing on inclusion size and corrosion-resistance of 304 stainless steel [J]. Mater. Sci. Technol., 2020, 36: 1263
|
10 |
Fan J W, He C C, Li J, et al. Effect of aging treatment on the pitting corrosion resistance of 2205 duplex stainless steel [J]. Shanghai Met., 2011, 33(4): 33
|
10 |
范君伟, 何晨冲, 李杰等. 时效处理对2205双相不锈钢耐点蚀性能的影响 [J]. 上海金属, 2011, 33(4): 33
|
11 |
Jastej S, Shahi A S. Impact toughness, fatigue crack growth and corrosion behavior of thermally aged UNS S32205 duplex stainless steel [J]. Trans. Indian Inst. Met., 2019, 72: 1497
|
12 |
Zhang L H. Study on the corrosion behavior of economical duplex stainless steel 2101 [D]. Shanghai: Fudan University, 2010: 43
|
12 |
张丽华. 经济型双相不锈钢2101的腐蚀行为研究 [D]. 上海: 复旦大学, 2010: 43
|
13 |
Zhang Y H, Hu Q, Dai M J, et al. Investigation of micro-electrochemical activities of oxide inclusions and microphases in duplex stainless steel and the implication on pitting corrosion [J]. Mater. Corros., 2020, 71: 876
|
14 |
Zhang Z Y, Han D, Jiang Y M, et al. Microstructural evolution and pitting resistance of annealed lean duplex stainless steel UNS S32304 [J]. Nucl. Eng. Des., 2012, 243: 56
|
15 |
Chen L D, Tan H, Wang Z Y, et al. Influence of cooling rate on microstructure evolution and pitting corrosion resistance in the simulated heat-affected zone of 2304 duplex stainless steels [J]. Corros. Sci., 2012, 58: 168
|
16 |
Lu S W, Hu Q, Liu J, et al. Parameter optimization for capillary microelectrode preparation [J]. J. Wuhan Univ. Sci. Technol., 2019, 42(4): 100
|
16 |
卢赛文, 胡骞, 刘静等. 毛细管微电极制备参数优化 [J]. 武汉科技大学学报, 2019, 42(4): 100
|
17 |
Zhang Z Y, Wang Z Y, Jiang Y M, et al. Effect of post-weld heat treatment on microstructure evolution and pitting corrosion behavior of UNS S31803 duplex stainless steel welds [J]. Corros. Sci., 2012, 62: 42
|
18 |
Zhang Z Y, Zhang H Z, Zhao H, et al. Effect of prolonged thermal cycles on the pitting corrosion resistance of a newly developed LDX 2404 lean duplex stainless steel [J]. Corros. Sci., 2016, 103: 189
|
19 |
Guo Y J, Sun T Y, Hu J C, et al. Microstructure evolution and pitting corrosion resistance of the Gleeble-simulated heat-affected zone of a newly developed lean duplex stainless steel 2002 [J]. J. Alloy. Compd., 2016, 658: 1031
|
20 |
Ha H Y, Jang M H, Lee T H, et al. Interpretation of the relation between ferrite fraction and pitting corrosion resistance of commercial 2205 duplex stainless steel [J]. Corros. Sci., 2014, 89: 154
|
21 |
Ha H Y, Jang M H, Lee T H, et al. Understanding the relation between phase fraction and pitting corrosion resistance of UNS S32750 stainless steel [J]. Mater. Charact., 2015, 106: 338
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|