中国腐蚀与防护学报  2017, Vol. 37 Issue (6): 567-574    DOI: 10.11902/1005.4537.2016.221
  研究报告 本期目录 | 过刊浏览 |
飞机起落架镀镉4130钢在甲酸钾溶液薄液膜下腐蚀电化学行为研究
林修洲1,2(), 杨丽2, 梅拥军3, 郑兴文1, 罗淑文3, 崔学军1,2
1 四川理工学院 材料腐蚀与防护四川省重点实验室 自贡 643000
2 四川理工学院材料科学与工程学院 自贡 643000
3 中国民航局第二研究所 成都 610041
Corrosion Electrochemical Behavior Beneath Thin Electrolyte Layer of Potassium Formate Solution of Cd-plated 4130 Steel Used for Aircraft Landing Gear
Xiuzhou LIN1,2(), Li YANG2, Yongjun MEI3, Xingwen ZHENG1, Shuwen LUO3, Xuejun CUI1,2
1 Materials Corrosion and Protection Key Laboratory of Sichuan Province, Sichuan University of Science & Engineering, Zigong 643000, China
2 School of Materials Science and Engineering, Sichuan University of Science & Engineering,Zigong 643000, China
3 The Second Research Institute of CAAC, Chengdu 610041, China
全文: PDF(2762 KB)   HTML
摘要: 

采用自制薄液膜腐蚀试验装置,研究了飞机起落架镀镉AISI 4130钢在低温除冰液 (主要成分甲酸钾) 薄液膜下的腐蚀电化学行为。结果表明:镀镉4130钢在甲酸钾溶液中的腐蚀过程主要受氧扩散控制,薄液膜下腐蚀产物沉积对腐蚀过程产生较大影响。液膜较厚 (≥240 μm) 时,液膜厚度变化对阴极极限扩散电流密度和溶液电阻影响不大;液膜较薄时,阴极极限扩散电流密度和溶液电阻随液膜厚度减小而增大。在相同液膜厚度下,镀镉4130钢腐蚀电位随溶液浓度增大而降低。在低浓度甲酸钾溶液中,镀镉4130钢腐蚀速率较低,腐蚀电位和腐蚀速率受液膜厚度影响不大。在高浓度甲酸钾溶液中,镀镉4130钢腐蚀电位随液膜厚度减小而正移;薄液膜下腐蚀速率明显高于全浸,且随液膜厚度减小先增大后减小,在液膜厚度约为150 μm时出现极大值。

关键词 镀镉4130钢甲酸钾溶液除冰液薄液膜腐蚀电化学    
Abstract

The Cd-plated AISI 4130 steel is being widely used for aircraft landing gear and potassium formate is the main composition of the common deicing fluid. Therefore, it is worthy to investigate the corrosion electrochemical behavior of Cd plated AISI 4130 steel beneath thin electrolyte layer of potassium formate solution at low temperature. Results showed that the corrosion process of the Cd-plated AISI 4130 steel in potassium formate solution is mainly controlled by the diffusion of dissolved oxygen, and influenced by the deposition of corrosion product beneath the thin electrolyte layer. When the thickness of the electrolyte layer is higher (240 μm or more), there is little influence of the thickness of the electrolyte layer on the cathodic limited diffusion current density and solution resistance. When the thickness of the electrolyte layer is thinner, the cathodic limited diffusion current density and solution resistance are increased with the decrease of the thickness of the electrolyte layer. For the same thickness of the electrolyte layer, the corrosion potential of the Cd-plated AISI 4130 steel decreases with the increase of solution concentration. For the dilute solutions, the corrosion rate of the Cd-plated AISI 4130 steel is lower, and the corrosion potential and corrosion rate are less affected by the thickness of the electrolyte layer. When the concentration of potassium formate solution is higher, the corrosion potential of the Cd-plated AISI 4130 steel is positively shifted with the decrease of the thickness of the electrolyte layer. The corrosion rate of the Cd-plated AISI 4130 steel beneath thin electrolyte layer is obviously higher than that of full immersion test, and the corrosion rate for the former case increased first and then decreased with the decreasing thickness of the electrolyte layer, and reached the maximum value when the thickness of the electrolyte layer is about 150 μm.

Key wordsAISI 4130 steel plated by cadmium    potassium formate solution    deicing fluid    thin electrolyte laye    corrosion electrochemistry
收稿日期: 2016-11-21     
ZTFLH:  TG172  
基金资助:国家自然科学基金 (U1333103和U1633118),四川省青年科技创新研究团队项目 (2016TD0024) 和四川理工学院人才引进项目 (2016RCL12)
作者简介:

作者简介 林修洲,男,1974年生,博士,教授

引用本文:

林修洲, 杨丽, 梅拥军, 郑兴文, 罗淑文, 崔学军. 飞机起落架镀镉4130钢在甲酸钾溶液薄液膜下腐蚀电化学行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 567-574.
Xiuzhou LIN, Li YANG, Yongjun MEI, Xingwen ZHENG, Shuwen LUO, Xuejun CUI. Corrosion Electrochemical Behavior Beneath Thin Electrolyte Layer of Potassium Formate Solution of Cd-plated 4130 Steel Used for Aircraft Landing Gear. Journal of Chinese Society for Corrosion and protection, 2017, 37(6): 567-574.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2016.221      或      https://www.jcscp.org/CN/Y2017/V37/I6/567

图1  薄液膜腐蚀试验装置示意图
图2  镀镉4130钢在不同厚度的25%甲酸钾薄液膜下的阴极极化曲线
图3  镀镉4130钢实验前后的表面形貌
图4  实验后试样表面EDS分析结果
图5  镀镉4130钢腐蚀电位与极限扩散电流密度随甲酸钾溶液浓度的变化
图6  镀镉4130钢腐蚀电位与极限扩散电流密度随薄液膜厚度的变化
图7  镀镉4130钢在不同厚度的25%甲酸钾溶液薄液膜下的电化学阻抗谱
图8  腐蚀体系的等效电路模型
Concentration of potassium formate Thickness of layer / μm RsΩcm2 RtΩcm2
5% 30 245.3 1002.0
90 106.1 833.9
150 86.6 1101.2
240 33.4 934.3
500 13.1 945.7
10000 11.0 1172.0
10% 30 177.6 976.7
90 89.5 1069.6
150 65.6 895.7
240 35.1 980.3
500 10.1 835.4
10000 9.3 831.0
25% 30 71.6 852.7
90 67.7 905.6
150 35.0 1003.0
240 27.4 716.0
500 19.0 801.5
10000 5.3 867.5
50% 30 53.5 535.2
90 43.7 486.3
150 20.6 310.5
240 19.7 453.9
500 6.5 631.4
10000 3.5 747.0
100% 30 41.2 414.3
90 39.6 357.4
150 27.6 335.8
240 18.3 491.5
500 8.6 568.0
10000 2.4 669.9
表1  EIS拟合得到的腐蚀体系部分参数值
图9  溶液电阻随薄液膜厚度的变化
图10  1/Rt随薄液膜厚度的变化
[1] Liu T Q.Material development used for aircraft landing gear [A]. Academic Conference of Chinese Society of Aeronautics and Astronautics[C]. Shenzhen, 2007(刘天琦. 飞机起落架用材发展 [A]. 大型飞机关键技术高层论坛暨中国航空学会2007年学术年会论文集[C]. 深圳, 2007
[2] Klein-Paste A, Huseby A B, Anderson J D, et al. Braking performance of commercial airplanes during operation on winter contaminated runways [J]. Cold Reg. Sci. Technol., 2012, 79/80: 29
[3] Security Division of Airport Department, CAAC. Field maintenance manual for the airfield field in civil airport [Z]. 2000(中国民用航空总局机场司安全保障处. 民用机场飞行区场地维护手册 [Z]. 2000)
[4] Harrigan E T.Research Results Digest 9 - Alternative aircraft and pavement deicers and anti-icing formulations with improved environmental characteristics [R]. Washington, DC: Transportation research board of the national academies, 2010
[5] Peng H Q, Xia Z X, Su Z L.Airworthiness certification of civil aero-chemicals in China[J]. Procedia Eng., 2011, 17(5): 633
[6] SAE AMS 1435-2010. Fluid, generic, deicing/anti-icing runways and taxiways AMS 1435-2010. Fluid, generic, deicing/anti-icing runways and taxiways[S]. 2010
[7] SAE AMS1431-2012. Compound, solid runway and taxiway deicing/anti-icing[S]
[8] GBT 25356-2010 Airport pavement deicing anti-icing fluid [S]BT 25356-2010 Airport pavement deicing anti-icing fluid [S]. Beijing: China Standard Press, 2010(GBT 25356-2010 机场道面除冰防冰液 [S]BT 25356-2010 机场道面除冰防冰液 [S]. 北京: 中国标准出版社, 2010)
[9] ASTM F 1111-08b(Reapproved 2013). Standard test method for corrosion of low-embrittling cadmium plate by aircraft maintenance chemicals F 1111-08b(Reapproved 2013). Standard test method for corrosion of low-embrittling cadmium plate by aircraft maintenance chemicals[S]. 2013
[10] MHT 6088-2012 Standard test method for corrosion of low-embrittling cadmium plate by aircraft maintenace chemicals [S]HT 6088-2012 Standard test method for corrosion of low-embrittling cadmium plate by aircraft maintenace chemicals [S]. Beijing: China Standard Press, 2012(MHT 6088-2012 飞机维护用化学品对低氢脆镀镉钢板腐蚀的试验方法 [S]HT 6088-2012 飞机维护用化学品对低氢脆镀镉钢板腐蚀的试验方法 [S]. 北京: 中国标准出版社, 2012)
[11] Huttunen-Saarivirta E, Kuokkala V T, Kokkonen J, et al.Corrosion effects of runway de-icing chemicals on aircraft alloys and coatings[J]. Mater. Chem. Phys., 2011, 126: 138
[12] Friedman P L, Shi X M.Assessing the impact of pavement de-icing products on aircraft and airfield infrastructure[J]. Airport Manage., 2009, 3(3): 223
[13] Lin X Z, Li Y, Mei Y J, et al.Research progress of corrosion of cadmium plated layer on aircraft caused by airfield pavement deicing fluid[J]. J. Sichuan Univ. Sci. Eng.(Nat. Sci. Ed.), 2014, 27(4): 1(林修洲, 李月, 梅拥军等. 机场道面除冰液对飞机镀镉层腐蚀的研究现状与进展[J]. 四川理工学院学报(自然科学版), 2014, 27(4): 1)
[14] Nishikata A, Ichihara Y, Hayashi Y, et al.Influence of electrolyte layer thickness and pH on the initial stage of the atmospheric corrosion of Iron[J]. J. Electrochem. Soc., 1997, 144: 1244
[15] Reminta E, Sutter E, Tribollet B, et al.A thin layer cell adapted for corrosion studies in confined aqueous environments[J]. Electrochim. Acta, 2007, 52: 715
[16] Simillion H, Van Der Steen N, Terryn H, et al. Geometry influence on corrosion in dynamic thin film electrolytes[J]. Electrochim. Acta, 2016, 209: 149
[17] Liu W J, Cao F H, Chen A N, et al.Corrosion behaviour of AM60 magnesium alloys containing Ce or La under thin electrolyte layers. Part 1: Microstructural characterization and electrochemical behavior[J]. Corros. Sci., 2010, 52: 627
[18] Liao X N, Cao F H, Zheng L Y, et al.Corrosion behaviour of copper under chloride-containing thin electrolyte layer[J]. Corros. Sci., 2011, 53: 3289
[19] Zhong X K, Zhang G A, Qiu Y B, et al.The corrosion of tin under thin electrolyte layers containing chloride[J]. Corros. Sci., 2013, 66: 14
[20] Huang H L, Pan Z Q, Guo X P, et al.Effects of direct current electric field on corrosion behaviour of copper, Cl- ion migration behaviour and dendrites growth under thin electrolyte layer[J]. Trans. Nonferrous Met. Soc. China, 2014, 24: 285
[21] Ding K K, Li X G, Xiao K, et al.Electrochemical migration behavior and mechanism of PCB-ImAg and PCB-HASL under adsorbed thin liquid films[J]. Trans. Nonferrous Met. Soc. China, 2015, 25: 2446
[22] Yi P, Xiao K, Ding K K, et al.In situ investigation of atmospheric corrosion behavior of PCB-ENIG under adsorbed thin electrolyte layer[J]. Trans. Nonferrous Met. Soc. China, 2016, 26: 1146
[23] Liu Z J, Wang W, Wang J, et al.Study of corrosion behavior of carbon steel under seawater film using the wire beam electrode method[J]. Corros. Sci., 2014, 80: 523
[24] Thee C, Hao L, Dong J H, et al.Atmospheric corrosion monitoring of a weathering steel under an electrolyte film in cyclic wet-dry condition[J]. Corros. Sci., 2014, 78: 130
[25] Tang Z L, Li C, Li H.Corrosion rate of carbon steel under liquid layer containing Cl- and its correlation with environment control factors[J]. J. Chin. Soc. Corros. Prot., 2010, 30: 67(唐子龙, 李超, 李辉. NaCl液膜下碳钢腐蚀速率及其与环境因素的关联性[J]. 中国腐蚀与防护学报, 2010, 30: 67)
[26] Lin X Z, Yang L, Du Y, et al. A kind of corrosion test device which can automatically control the thickness of the thin electrolyte layer [P]. Chinese patent: ZL 201520578261.1, 2016-01-20(林修洲, 杨丽, 杜勇等. 一种可自动控制液膜厚度的薄液膜腐蚀试验装置 [P]. 中国专利: ZL 201520578261.1, 2016-01-20)
[27] Yang L, Lin X Z, Mei Y J, et al.Corrosion behaviors of carbon steel under 3.5% NaCl thin liquid film[J]. J. Sichuan Univ. Sci. Eng.(Nat. Sci. Ed.), 2015, 28(3): 1(杨丽, 林修洲, 梅拥军等. 3.5%NaCl薄液膜下碳钢的腐蚀行为研究[J]. 四川理工学院学报(自然科学版), 2015, 28(3): 1)
[28] MIL-STD-870 C-2007, Cadmium Plating, Low Embrittlement, Electrodeposition[S]. 2007
[29] Cole I S, Ganther W D, Sinclair J D, et al.A study of the wetting of metal surface in order to understand the processes controlling atmospheric corrosion[J]. J. Electrochem. Soc., 2004, 151(12): B627
[30] An B G, Zhang X Y, Han E-H, et al.Corrosion of zinc in simulated acid rain solution and under thin electrolyte layer formed by simulated acid rain solution[J]. Acta Metall. Sin., 2004, 40: 202(安百刚, 张学元, 韩恩厚等. Zn在模拟酸雨溶液中及其液膜下的腐蚀[J]. 金属学报, 2004, 40: 202)
[1] 赵苇杭, 王浩伟, 蔡光义, 董泽华. AA6061铝合金在含盐薄液膜下的局部腐蚀与缓蚀机理[J]. 中国腐蚀与防护学报, 2017, 37(4): 366-374.
[2] 陈启萌,张俊喜,原徐杰,戴念维. 外加交流电场对薄液膜中氧扩散的影响[J]. 中国腐蚀与防护学报, 2015, 35(6): 549-555.
[3] 鞠玉琳, 李焰. 气相缓蚀剂的研究进展[J]. 中国腐蚀与防护学报, 2014, 34(1): 27-36.
[4] 唐子龙, 李辉, 李超. Na2SO4液膜下碳钢早期腐蚀速率及其环境因素的关联性[J]. 中国腐蚀与防护学报, 2010, 30(3): 217-221.
[5] 唐子龙;李超;李辉. NaCl液膜下碳钢腐蚀速率及其与环境因素的关联性[J]. 中国腐蚀与防护学报, 2010, 30(1): 67-71.
[6] 唐子龙 李超 曲文超 宋鑫. 污染离子对Q235钢潮湿时间的多因素关联性分析[J]. 中国腐蚀与防护学报, 2009, 29(6): 426-430.
[7] 唐子龙 宋鑫 张义萍. 纯水薄液膜下Q235钢潮湿时间的影响因素和腐蚀速度的磁阻研究[J]. 中国腐蚀与防护学报, 2009, 29(3): 161-166.
[8] 余润兰 . 铁闪锌矿的腐蚀电化学研究[J]. 中国腐蚀与防护学报, 2004, 24(4): 226-229 .