含Cr油套管钢CO2腐蚀产物膜特征

陈长风;赵国仙;严密林

西北工业大学材料科学与工程学院

CHARACTERISTICS OF CO2 CORROSION SCALES ON Cr-CONTAINING N80 STEEL

Changfeng Chen;Guoxian Zhao;Milin Yan

西北工业大学材料科学与工程学院

全文: PDF(143 KB)

摘要: 在模拟油田CO2腐蚀环境下，利用XRD、EDS、XPS和SEM研究了含Cr的N80钢腐蚀产物膜的特征.结果表明，本试验条件下Cr在腐蚀产物膜中富积，形成非晶态物质Cr(OH)3，使得腐蚀产物膜具有阳离子选择性，阳极反应受到抑制，腐蚀速率降低.

关键词 ： CO2腐蚀, 腐蚀产物膜, 含Cr的N80钢

Abstract：While simulating the CO2 corrosion environment in oilfield,the XRD，EDS,XPS and SEM techniques were adopted to study the characte ristics of CO2 corrosion scales on N80 steel containing Cr.The results demonst rated that Cr could be enriched in corrosion scales forming amorphous compound C r(OH)3,which made the corrosion scale has the character of cation-selectivity. This cation-selective scale could block anions such as Cl-,CO2-3 and H CO -3 penetrating the corrosion scale and decrease the anionic concentration at the interface between matrix and corrosion scale.As a result,the anodic reactio ns could be suppressed and corrosion rate be reduced.

Key words： CO2 corrosion Cr-containing N80 steel corrosion scal es

收稿日期: 2001-03-25

ZTFLH:

TG174

通讯作者: 陈长风

Corresponding author: Changfeng Chen

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陈长风
	赵国仙
	严密林
44.8K

引用本文:

陈长风; 赵国仙; 严密林 . 含Cr油套管钢CO2腐蚀产物膜特征[J]. 中国腐蚀与防护学报, 2002, 22(6): 335-338 .
Changfeng Chen, Guoxian Zhao, Milin Yan. CHARACTERISTICS OF CO2 CORROSION SCALES ON Cr-CONTAINING N80 STEEL. J Chin Soc Corr Pro, 2002, 22(6): 335-338 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I6/335

[1]ZhangXY ,DiC ,LeiLC .CO2CorrosionandControl[M ].Beijing:ChemicalIndustryPress,2000(张学元,邸超,雷良才.二氧化碳腐蚀与控制[M ].北京:化学工业出版社,2000)
[2]NyborgR ,DugstadA .MesaCorrosionattackcarbonsteeland05%chromiumsteel[A].Corrosion/98[C].1998,29
[3]InabaH ,KimuraM ,YokokawaH .Ananalysisofthecorrosionre sistanceoflowchromium-steelinawetCO2 environmentbytheuseofanelectrochemicalpotentialdiagram[J].Corros.Sci.,1996,38(9):1449
[4]KirchheimR ,HeineB ,FischmeisterH ,etal.Thepassivityofiron-chromiumalloys[J].Corros.Sci.,1989,29(7):899
[5]IkedaA ,UedaM .PredictingCO2CorrosionintheOilandGasIn dustry[M].London,UK :TheInstituteofMaterials,1994,59-93
[6]Al-HassanS ,MishraB ,OlsonDL ,etal.Effectofmicrostructureoncorrosionofsteelsinaqueoussolutioncontainingcarbondioxide[J].Corrosion,1988,54(6):480
[7]ChenCF ,ZhaoGX ,YanML ,etal.StudyofCO2 corrosionscalesonN80steel[J].J .ChineseSocietyforCorrosionandProtection,2002,22(3):143-147(陈长风,赵国仙,严密林.N80钢CO2腐蚀产物膜研究[J].中国腐蚀与防护学报,2002,22(3):143-147)
[8]PalaciosCA ,ShadleyJR .CharacteristicsofcorrosionscalesonsteelsinaCO2-saturatedNaClBrine[J].Corrosion,1991,47(2):122
[9]LinterBR ,BursteinGT .Reactionofpipelinesteelsincarbondiox idesolutions[J].Corros.Sci.,1999,42(2):117
[10]OgundeleGI,WhiteWE .Someobservationoncorrosionofcar bonsteelinaqueousenvironmentscontainingcarbondioxide[J].Corrosion,1986,42(2):71
[11]CroletJL ,BonisMR .PHmeasurementsinaqueousCO2 solutionunderhighpressureandtemperature[J].Corrosion,1983,39(2):39-46
[12]ShanghaiPharmaceuticalIndustryDesignInstitute.HandbookforChemicalEngineeringTechnologyDesign[M ].Beijing:ChemicalIndustryPress,1996,2-364(上海医药设计院编.化工工艺设计手册[M ].北京:化学工业出版社,1996,2-364)
[13]BrooksAR ,ClaytonCR ,DossK ,LuYC .OntheroleofCrinthepassivityofstainlesssteel[J].JournalofElectrochemicalSociety,1986,133(12):2459-2464

[1]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[2]	黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[3]	鲍明昱, 任呈强, 胡静思, 刘博, 李佳蒙, 王丰, 刘丽, 郭小阳. 油气管材应力诱导腐蚀电化学行为探讨[J]. 中国腐蚀与防护学报, 2017, 37(6): 504-512.
[4]	张弟,梁平,张云霞,史艳华,秦华. 库尔勒土壤模拟溶液中形成的腐蚀产物膜对X80钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[5]	董洋洋, 黄峰, 程攀, 胡骞, 刘静. X65 MS耐酸管线钢在H₂S环境中腐蚀产物膜的演变[J]. 中国腐蚀与防护学报, 2015, 35(5): 386-392.
[6]	梁平, 王莹. 覆有短期腐蚀产物膜的X80钢的电化学行为[J]. 中国腐蚀与防护学报, 2013, 33(5): 371-376.
[7]	俞芳高克玮路民旭. 流动状态下X65管线钢CO₂腐蚀产物膜结构和力学性能的评价[J]. 中国腐蚀与防护学报, 2009, 29(6): 401-404.
[8]	李桐; 高克玮; 路民旭 . X65钢CO2腐蚀产物膜形成机理研究[J]. 中国腐蚀与防护学报, 2007, 27(6): 338-341 .
[9]	马文海; 裴晓含; 高飞; 高纯良 . N80钢在模拟深层气井水溶液中的CO2腐蚀行为[J]. 中国腐蚀与防护学报, 2007, 27(1): 8-13 .
[10]	赵国仙; 吕祥鸿; 李鹤林; 路民旭 . 温度对P110钢CO2腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2005, 25(2): 93-96 .
[11]	林冠发 . CO2压力对金属腐蚀产物膜形貌结构的影响[J]. 中国腐蚀与防护学报, 2004, 24(5): 284-288 .
[12]	陈长风; 路民旭; 赵国仙 . 含1%Cr的N80钢CO2腐蚀产物膜特征[J]. 中国腐蚀与防护学报, 2003, 23(6): 330-334 .
[13]	陈长风; 路民旭; 赵国仙 . 腐蚀产物膜覆盖条件下油套管钢CO2腐蚀电化学特征[J]. 中国腐蚀与防护学报, 2003, 23(3): 139-143 .
[14]	陈长风; 路民旭; 赵国仙 . N80油管钢CO2腐蚀点蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(1): 21-25 .
[15]	赵国仙; 陈长风; 路民旭 . CO2腐蚀的产物膜及膜中物质交换通道的形成[J]. 中国腐蚀与防护学报, 2002, 22(6): 363-366 .

Viewed

Full text

Abstract

Cited

Shared

Discussed